外文摘要：XPS results demonstrate that Si69 can be chemically combined with carbon black to some extent。 When Si69 was added to the compounds， the vulcanization were restrained， but with improved properties including tensile strength 300% modulus of vulcanizates were also obtained while the tear strength was reduced。 The DMA results showed the application of Si69 in carbon black filled NR/BR/NBR blends could effectively reduce the rolling resistance without the sacrifice of wet grip。