Twist Angle Dependence of Interfacial Fracture Toughness of (0001) Twist Boundary of Alumina

扫码查看

原文链接

NETL

外文摘要：The influence of the twist angle on the fracture toughness of (0001) twist boundary of alumina was investigated using alumina bicrystals。 The alumina bicrystals were fabricated by joining two single crystals which were rotated relative to each other around the <0001> axis with the specific twist angles。 Interfacial fracture toughness of alumina bicrystals was measured by single edge V-notched tension test。 It was shown that the fracture toughness of (0001) twist boundary of alumina varied from 1 Jm~(-2) to 22Jm~(-2) depending on the twist angle。 Furthermore， the interfacial fracture toughness also depended on the crack propagating direction。 The experimental results were discussed in relation to the change in surface energy， boundary energy and plastic dissipative energy。

外文关键词：

fracture toughnessalumina bicrystal(0001) twist boundarytwist angle

作者：

K. Yasuda、J. Tatami、T. Harada、Y. Matsuo

展开 >

作者单位：

Tokyo Institute of Technology, 2-12-1, Ookayama, Meguro-ku, Tokyo, 152-8552, Japan

Now with Department of Materials Chemistry, Yokohama National University, 79-5, Tokiwadai, Hodogayaku, Yokohama, 240-8501, Japan

会议名称：

International symposium on the science of engineering ceramics;EnCera'98;International conference on high temperature ceramic matrix composites;HT-CMC 3

会议地点：

Osaka(JP);Osaka(JP);Osaka(JP);Osaka(JP)

会议母体文献：

The science of engineering ceramics II

页码：

573-576

出版时间：

1998