查看更多>>摘要：The crack-closure effect is a crucial factor that affects the crack growth rate and should be considered in simula-tion analysis and testing.A mixed-mode Ⅰ+Ⅱ loading fatigue crack growth test was performed using EA4T axle steel specimens.The variation of the plastic-induced crack closure(PICC)effect and the roughness-induced crack closure(RICC)effect during crack deflection in the mixed-mode is examined in this study.The results show that the load perpendicular to the crack propagation direction hinders the slip effect caused by the load parallel to the crack propagation direction under mixed-mode loading,and the crack deflection is an intuitive manifestation of the inter-action between the PICC and RICC.The proportion of the RA value change on the crack side caused by contact friction was reduced by the interaction between PICC and RICC.The roughness of the crack surface before and after the crack deflection is different,and the spatial torsion crack surface is formed during the crack propagation process.With the increase of the crack length,the roughness of the fracture surface increases.During the crack deflection process,the PICC value fluctuates around 0.2,and the RICC value is increased to 0.15.
查看更多>>摘要：With the growing interest in utilizing Mg and austenitic stainless steel(ASS)in the automotive sector,joining them together in three-sheet configuration is inevitable.However,achieving this task presents considerable challenges due to the large differences in their physical,metallurgical and mechanical properties.To overcome these chal-lenges,the feasibility of using weld-bonding to join Mg alloy/ASS/ASS was investigated.The nugget formation,interface characteristics,microstructure and mechanical properties of the joints were investigated.The results show that the connection between the Mg alloy and upper ASS was achieved through the combined effect of the cured adhesive and weld-brazing in the weld zone.On the other hand,a metallurgical bond was formed at the ASS/ASS interface.The Mg nugget microstructure exhibited fine columar grains composed predominantly of primary α-Mg grains along with a eutectic mixture of α-Mg and β-Mg17Al12.The nugget formed at the ASS/ASS interface consisted largely of columnar grains of austenite,with some equiaxed dendritic grains formed at the centerline of the joint.The weld-bonded joints exhibited an average peak load and energy absorption of about 8.5 kN and 17 J,respectively(the conventional RSW joints failed with minimal or no load application).The failure mode of the joints changed with increasing welding current from interfacial failure via the Mg nugget/upper ASS interface to partial interfacial failure(part of the Mg nugget was pulled out of the Mg sheet).Both failure modes were accompanied by cohesive failure in the adhesive zone.
万方数据
维普