为提高Cu、Ag、La2O3的界面结合强度,通过化学镀工艺在Ag、La2O3粉末表面镀上均匀、完整和致密的Cu粉.采用热压烧结工艺制备出含有不同成分的三层和五层Ag/Cu/La2O3功能梯度材料,研究成分对两种功能梯度材料的显微组织、致密度和润湿性的影响.
Preparation and Properties of Cu-Ag-La2O3 Functionally Gradient Materials
In order to improve the interfacial bonding strength of Cu,Ag,La2O3,uniform,complete and compact Cu powder was coated on the surface of Ag and La2O3 powder by electroless plating process.Three layers and five layers Ag/Cu/La2O3 functionally graded materials with different compositions were prepared by hot pressing sintering process.The effects of compositions on the microstructure,density and wettability of the two functionally graded materials were stud-ied.

electroless plating processhot pressing sinteringfunctional gradient materialsdensification

杨李林、王佳杰、郑浩、张绍峰、黄晓晨

展开 >

蚌埠学院材料与化学工程学院,安徽蚌埠 233030

化学镀工艺 热压烧结工艺 功能梯度材料 致密度

安徽省科学研究重大项目国家级大学生创新创业训练计划国家级大学生创新创业训练计划省级大学生创新创业训练计划煤清洁转化与高值化利用安徽省重点实验室开放基金安徽省自然科学基金面上项目

KJ2021ZD0141202111305001202111305005S202111305006CHV19-052208085ME104

2024

10.3969/j.issn.1008-553X.2024.01.015

安徽化工
安徽省化工研究院

安徽化工

影响因子：0.229
ISSN：1008-553X
年,卷(期)：2024.50(1)
  • 15