Study on the high-temperature properties of heat-resistant steel 309S
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
万方数据
维普
The properties of heat-resistant steel 309S at elevated properties were investigated.The results revealed a rapid decrease in the short-time tensile strength at elevated temperatures.At 1 000 ℃,the yield strength and tensile strength are 14％and 7％of their respective values at room temperature,respectively.The creep rupture strength was inferred in terms of the relationship between stress and duration time at high temperatures.After 1 000 h,the creep rupture strength is 37.98 MPa at 800℃,12.63 MPa at 900 ℃,and 7.27 MPa at 1 000 ℃.The fractures occurring at these high temperatures were intergranular in nature.Under the experimental condition,the fatigue limit stress is 25 MPa.The number of fatigue cycles and crack growth time decrease with increasing stress.Fracture morphology analysis shows that the fatigue cracks initiate on the surface of the sample and propagate through transgranular expansion.
strength at elevated temperaturecreep rupture strengthfatigue limit stress
HUANG Junxia、BI Hongyun、LI Shi
展开 >
Research Institute,Baoshan Iron & Steel Co.,Ltd.,Shanghai 201999,China
万方数据
维普