Simple preparation of C(CS)/g-C3N4/Co carbon aerogel and its catalytic performance for ammonium perchlorate

扫码查看
原文链接
  • 万方数据
Biomass chitosan(CS)was used as a template,graphitic phase carbon nitride(g-C3N4)with high nitrogen content and certain catalytic activity was used as a dopant,and nano-transition metal cobalt(Co)was used as a catalytic center point.The carbon aerogel(C(CS)/g-C3N4/Co)with a three-dimensional network-like structure was prepared by assembling the three materials through experimental opera-tions such as freeze-drying and high-temperature carbonization.It was demonstrated by scanning and transmission characterization that the CS in the carbon aerogel could provide more active sites for the cobalt nanoparticles,and the doping of graphite-phase carbon nitride as a template dispersed the cobalt nanoparticles and changed the conductivity of the CS.To investigate the catalytic effect of carbon aerogel on ammonium perchlorate(AP),it was investigated by differential thermal analyzer and TG thermal analysis.This carbon aerogel was very effective in catalyzing AP,and the 10 wt％content of the catalyst reduced the AP pyrolysis peak from 703.9 to 595.5 K.And to further investigate the synergistic effect of the three materials,further carbon aerogels such as C(CS)/Co,g-C3N4/Co were prepared and applied to catalyze AP,and the same ratio reduced the AP pyrolysis peak by 98.1 ℃ and 97.7 ℃.This result indicates a synergistic effect of the assembly of the three materials.

g-C3N4ChitosanCoAmmonium perchloratePyrolysis kinetics

Yujie Yan、Bo Jin、Rufang Peng

展开 >

State Key Laboratory of Environment-friendly Energy Materials,School of Materials Science and Engineering,Southwest University of Science and Technology,Mianyang,621010,China

Natural Science Foundation of ChinaOutstanding Youth Science and Technology Talents Program of SichuanOpen Project of State Key Laboratory of Environmentfriendly Energy Materials(Southwest University of Science and Technology)

2187519219JCQN008522fksy18

2024

10.1016/j.dt.2023.04.011

防务技术
中国兵工学会

防务技术

CSTPCD
影响因子：0.358
ISSN：2214-9147
年,卷(期)：2024.33(3)
  • 33