In a solution treated Co-20Ni-6Si shape memory alloy,coherent nano-particles were precipitated after annealing at 873 K for 1 min,but the shape memory effect almost vanished.It is attributed to that the coherent nano-particles not only suppressed the stress-induced face-centered cubic to close-packed hexagonal martensite transformation but also damaged the crystallographic reversibility of reverse martensite transformation.After further annealing at 1073 K for 1 min,the shape memory effect was reju-venated owing to the dissolution of nano-particles.Besides,the recovery strain significantly increased to 5.1％ from the solution treatment of 3.1％ after annealing at 1073 K for 1 min.