Abstract
The effect of aging treatment on the microstructure and corrosion behavior of a Fe-18Cr-15Mn-0.66N high-nitrogen stainless steel(HNSS)in 3.5 wt.％NaCl solution was investigated using a series of elec-trochemical tests,scanning electronic microscopy(SEM),X-ray diffraction(XRD)and X-ray photoelectron spectroscopy(XPS).The results showed that the aging treatment led to the precipitation of Cr2N parti-cles along the grain boundaries and their morphologies changed from dispersive particles to continuous network as the aging time increased up to 60 min.Aging time had minor effects on the corrosion poten-tial and corrosion current density,but resulted in the sharp decrease in the pitting corrosion potential.The passive film behaved as a n-type semiconductor,and the donor density of the passive film increased with the aging time.Meanwhile,the fraction of stable oxide(Cr2O3)in the passive film decreased with the aging time.It demonstrates that the aging treatment deteriorated the protectiveness of the passive film,hence weakened the corrosion resistance of HNSS.
基金项目
National Nat-ural Science Foundation of China(52001142)
National Nat-ural Science Foundation of China(52005228)
National Nat-ural Science Foundation of China(51801218)
National Nat-ural Science Foundation of China(51911530211)
National Nat-ural Science Foundation of China(51905110)
Science Foundation of Jiangsu Province(BK20180984)
NETL
NSTL
维普
万方数据