酸性光亮电镀锡铈合金工艺的研究
Electroplating Technology of Bright Acidic Sn-Ce Alloy
迟红训 1宫胜臣 1卢声 1王东东 1左华龙1
作者信息
- 1. 辽东学院化工与材料学院，辽宁丹东 118003
- 折叠
摘要
采用赫尔槽试验研究了镀液中各种成分的作用及工艺条件，用扫描电镜（ SEM ）观察了镀层形貌。研究发现，在酸性光亮镀锡镀液中添加铈盐和自制的光亮剂，可获得一种铈含量达0．5％的锡铈合金镀层，该镀层外观光亮、平整。通过镀层性能测试，并与纯锡镀层性能进行比较，发现：当镀层厚度大于5μm时，锡铈合金镀层表面致密均匀，结晶细致光亮；其抗氧化性、耐蚀性、防变色性能及可焊性明显优于纯锡镀层，解决了纯锡镀层在焊锡时易发生变色，提高了焊接温度。
Abstract
With Hull cell experiment , the function component in the bath and technological conditions of bright acidic Sn-Ce alloy were studied .The appearance of deposits was tested by SEM .It was found that a smooth and bright plating layer of Sn -Ce alloy with 0 .5% Ce was obtained by adding cerium salt and the homemade brightener in the tin electroplating bath .The coating was tested and compared with pure tin electroplating plating . The results showed that when the plating was thicker than 5μm, the surface of the Sn -Ce alloy plating was uniform and dense with fine and bright crystals .It was more antioxidant , corrosion-resistant, solderable and resistant to change color than pure tin plating .
关键词
锡铈合金镀层/抗氧化性/耐蚀性/可焊性Key words
Sn-Ce alloy electroplating plating/antioxidation/corrosion resistance/solderability引用本文复制引用
出版年
2014
NETL
NSTL
维普
万方数据