本文研究了掺氢天然气直接内重整平管型固体氧化物电池短堆的长期稳定性和衰减机理.通过约3000小时的实测实验,结果显示,电堆的总体衰减率为 2.3％kh-1,电堆中三个金属连接板的面积比电阻分别增加了0.276 Q.cm2、0.254 Q·cm2和0.249 Ω·cm2,但电堆中两个电池的电压反而分别增加了3.38 mV·kh-1和3.78 mV·kh-1.电堆衰减主要由金属连接件表层氧化及其与阴极集流层材料反应生成SrCrO4物质,两者共同作用增大了电池与金属连接体间的界面电阻所致.结果表明,以掺氢天然气为燃料直接内重整平管型固体氧化物燃料电池电堆具有良好的稳定性.本文工作为掺氢天然气在固体氧化物燃料电池堆中的直接内重整应用提供了理论参考与实验依据.
Stability of a Solid Oxide Cell Stack under Direct Internal-reforming of Hydrogen-blended Methane
In this work,the long-term stability and degradation mechanism of a direct internal-reforming solid oxide fuel cell stack(IR-SOFC stack)using hydrogen-blended methane steam reforming were investigated.An overall degradation rate of 2.3％.kh-1 was found after the stack was operated for 3000 hours,indicating a good long-term stability.However,the voltages of the two cells in the stack were increased at the rates of 3.38 mV kh-1 and 3.78 mV·kh-1,while the area specific resistances of the three metal interconnects in the stack were increased to 0.276 Ω·cm2,0.254Ω·cm2 and 0.249 Ω·cm2.The degradation of the stack might be caused by segregation of chromium on the surface of metal interconnects and the formation of SrCrO4 insulating phase in the current collecting layer of the cathode,which result in an increase in the interfacial resistance and a decrease in the stack performance.The long-term performance of a flat-tube IR-SOFC stack could be further improved by suitably coating the metal interconnect surface.This work provides theoretical and experimental guideline for the application of hydrogen-blended methane steam reforming in flat-tube IR-SOFC stacks.

Hydrogen-blended methane steamInternal-reformingStabilitySolid oxide fuel cell stack

汤亚飞、武安祺、韩贝贝、刘华、包善军、林王林、陈铭、官万兵、Subhash C.Singhal

展开 >

中国科学院宁波材料技术与工程研究所,浙江宁波 315201

浙江启明电力集团有限公司,浙江 舟山 316099

浙江大学舟山海洋研究中心,浙江舟山 316021

丹麦技术大学能源转换与储存系,丹麦哥本哈根

展开 >

掺氢天然气 内重整 稳定性 固体氧化物电堆

国家重点研发计划国家自然科学基金国家自然科学基金Key R & D projects in Zhejiang ProvinceNingbo Key Research and Development project

2022YFB4003602U20A20251119320052021C011012023Z145

2024

10.61558/2993-074X.3430

电化学
中国化学会

电化学

CSTPCD北大核心
影响因子：0.263
ISSN：1006-3471
年,卷(期)：2024.30(1)
  • 34