聚丁二酸丁二醇酯对聚乳酸基木塑复合材料性能的影响
Effect of polybutylene succinate on properties of polylactic acid-based wood-plastic composites
刘杰 1赵雪松 2李奇 1韦东山 3雷志涛 1张志远1
作者信息
- 1. 内蒙古农业大学 材料科学与艺术设计学院,呼和浩特 010018;内蒙古自治区沙生灌木资源纤维化和能源化开发利用重点实验室,呼和浩特 010018
- 2. 内蒙古农业大学 机电工程学院,呼和浩特 010018
- 3. 内蒙古农业大学 林学院,呼和浩特 010018
- 折叠
摘要
为解决聚乳酸(PLA)基木塑复合材料制备成本高、韧性和耐热性差等问题,以可降解树脂聚丁二酸丁二醇酯(PBS)作为改性树脂,与沙柳木粉(WF)和 PLA共混复合,通过模压法制备环境友好型 PBS-WF/PLA三元可降解木塑复合材料.研究结果表明:PBS的加入,可使复合材料的韧性、耐热性及热稳定性提高,但强度和刚度下降.当PBS加入量为树脂总量的 50wt%时,PBS-WF/PLA复合材料的综合性能相对较佳,与WF/PLA相比,生产成本降低约 20%,PBS-WF/PLA的静曲强度、弹性模量和拉伸强度的保持率分别为 86.5%、63.8%和 73.1%,冲击强度提高 40.1%,维卡软化温度、热变形温度和第二阶段热分解起始温度分别升高 37.1℃、53.7℃和4.1℃.
Abstract
In order to solve the problems of high preparation cost,poor toughness and heat resistance of polylactic acid(PLA)-based wood-plastic composites,biodegradable resin polybutylene succinate(PBS)was used as a modi-fied resin,which was blended with Salix powder(WF)and PLA to prepare environmentally friendly PBS-WF/PLA ternary degradable wood-plastic composites by compression molding.The results show that the addition of PBS can improve the toughness,heat resistance and thermal stability of the composites,but the strength and stiffness decrease.When the addition amount of PBS is 50wt%of the total resin,the comprehensive properties of PBS-WF/PLA composites are relatively better.Compared with WF/PLA,the production cost is reduced by about 20%.The retention rates of static bending strength,elastic modulus and tensile strength of PBS-WF/PLA are 86.5%,63.8%and 73.1%,respectively.The impact strength is increased by 40.1%,and the Vicat softening temperature,thermal deformation temperature and the initial temperature of the second stage of thermal decomposition are increased by 37.1℃,53.7℃and 4.1℃,respectively.
关键词
聚丁二酸丁二醇酯/聚乳酸/木塑复合材料/力学性能/热性能Key words
polybutylene succinate/polylactic acid/wood plastic composites/mechanical properties/thermal performance引用本文复制引用