采用熔融共混制备了聚对苯二甲酸-己二酸丁二酯(poly(butylene adipate-co-terephthalate),PBAT)与聚3-轻基丁酸酯4-经基丁酸酯(poly(3-hydroxybutyrate-co-4-hydroxybutyrate),P34HB)的共混材料.研究了P34HB含量(0wt％,5wt％、10wt％、15 wt％、20 wt％)对共混材料熔体流动性能、力学性能、热性能和界面微观形貌的影响,及其PBAT/P34HB吹塑薄膜的力学性能和氧气阻隔性能.结果表明,P34HB的加入降低了材料的熔体黏度,提高了材料的流动性以及薄膜的直角撕裂性能、穿刺性能和氧气阻隔性能.当P34HB含量为5 wt％时,共混材料综合性能最佳,两相相容性良好,共混材料和吹塑薄膜均具有优异的力学性能,薄膜的拉伸性能和穿刺强度最高,是性能优异的包装和农膜材料.
Preparation and Characterization of Poly(butylene adipate-co-terephthalate)/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate)Blends
The blends of poly(butylene adipate-co-terephthalate)(PBAT)/poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P34HB)were prepared by melt-compounding.The effects of P34HB content(0 wt％,5 wt％,10 wt％,15 wt％,20 wt％)on the melt flowability,tensile properties,thermal behavior and interfacial morphology of the blends were investigated.The mechanical properties and barrier properties of the blown films were also studied.The results indicated that the incorporation of P34HB increased the melt flowability of PBAT,improved the right-angle tear strength,puncture strength and oxygen barrier property of blown films.When the weight content of P34HB is 5 wt％,the blend exhibited the highest comprehensive performance,PBAT and P34HB showed good compatibility,the blend displayed excellent mechanical properties for both injection samples and blown films,and the film demonstrated the highest tensile and puncture strength,showing promising application prospects for package and agriculture film.

Poly(butylene adipate-co-terephthalate)Biodegradable materialMechanical propertyBarrier propertyPoly(3-hydroxybutyrate-co-4-hydroxybutyrate)

肖湘莲、尹琳丽、张熙柏、雷雅芳、杨义浒、陈锐、周超、张向南、黄建平

展开 >

湖南工学院材料科学与工程学院,衡阳 421002

深圳光华伟业股份有限公司,深圳 518057

孝感易生新材料有限公司,孝感 432100

聚对苯二甲酸-己二酸丁二酯 生物降解材料 力学性能 阻隔性能 聚3-羟基丁酸酯4-羟基丁酸酯

广东省企业科技特派员专项资助项目湖南省教育厅重点项目湖南省教育厅重点项目国家级大学生创新创业训练计划项目湖南省应用特色学科湖南省应用特色学科开放基金湖南工学院校级重点自科项目

GDKTP202105330021A056920A137202211528031湘教通[2022]351号KFB22005HY22025

2024

10.14028/j.cnki.1003-3726.2024.23.245

高分子通报
中国化学会 中国科学院化学研究所

高分子通报

CSTPCD北大核心
影响因子：0.63
ISSN：1003-3726
年,卷(期)：2024.37(3)
  • 28