Investigating effect of coke porosity on blast furnace performance based on multi-physical fields

扫码查看
原文链接
  • NETL
  • NSTL
  • 万方数据
Reducing coke use is an effective measure to reduce carbon emission and energy consumption in the blast furnace(BF)ironmaking.Essentially,BF is a high-temperature moving bed reactor,where complex physical transformations coupled with complicated reactions occur.This makes it challenging to investigate the factors determining BF performance with the conventional method.A multi-physical field coupling mathematical model of BF was thus developed to describe its mass and heat transfer as well as its intrinsic reactions.Then,the proposed model was validated with the production data.Under coupling conditions,influences of dominating reactions on BF performance(temperature distribution,gas distribution,iron formation reaction,and direct reduction degree)were revealed.The results indicated that coke combustion,indirect reduction,and direct reduction of iron ore mainly took place nearby the shaft tuyere,cohesive zone,and dripping zone,respectively.Besides,the rate of coke solution loss reaction was increased with the rising coke porosity in the cohesive zone.Considering the effect of coke porosity on the efficiency and stability of BF,the coke porosity of 0.42 was regarded as a reasonable value.

Blast furnaceMathematical modelMulti-physical fieldSimulationCoke porosity

Ji Chen、Zhao Lei、Zhe Yao、Li Wang、Qiang Ling、Ping Cui

展开 >

Anhui Province Key Laboratory of Coal Clean Conversion and High Valued Utilization,School of Chemistry and Chemical Engineering,Anhui University of Technology,Ma'anshan 243002,Anhui,China

Shanxi Academy of Printing Technology Research Institute Co.,Ltd.,Xi'an 710077,Shaanxi,China

National Natural Science Foundation of ChinaNational Natural Science Foundation of ChinaNatural Science Foundation of Anhui Provincial Education DepartmentNatural Science Foundation of Anhui ProvinceAnhui Provincial Postdoctoral Science Foundation

2227800121776002KJ2021A04072008085QB872021B538

2024

10.1007/s42243-023-01045-w

钢铁研究学报(英文版)
钢铁研究总院

钢铁研究学报(英文版)

CSTPCD
影响因子：0.584
ISSN：1006-706X
年,卷(期)：2024.31(2)
  • 30