首页|Solidification crack characteristics and sensitivity of peritectic steel
Solidification crack characteristics and sensitivity of peritectic steel
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
万方数据
The characteristics and sensitivity of solidification cracks in peritectic steels were investigated using directional solidifi-cation technology.Interdendritic cracks were observed in both hypoperitectic steels(12CrlMoV,15CrMo)and hyper-peritectic steel(20CrMo)during solidification at growth velocities of 15,50,and 80 pm/s.At the dendritic boundaries,sulphide precipitates were found,promoting crack formation.Based on the statistical analysis of interdendritic cracks in peritectic steels,the area ratio(RA)of interdendritic cracks in a directional solidification structure was proposed to evaluate the crack sensitivity of peritectic steels.Furthermore,the crack sensitivities of peritectic steels(12CrlMoV,15CrMo,and 20CrMo)were tested,evaluated,and compared with the surface crack rates of three types of steels produced from a steel plant.The results demonstrated that RA was in good agreement with that of the steel plant,and the crack sensitivity of 12CrlMoV steel was the strongest,followed by that of 15CrMo and 20CrMo steels.Thus,RA can be used to evaluate the crack sensitivity of peritectic steel.
Ya-qiang Li、Jian-hua Liu、Zi-ming Wang、Ying-ying Li、Yang He、Xiao-wei Li
展开 >
Department of Automotive Engineering,Hebei Vocational University of Technology and Engineering,Xingtai 054000,Hebei,China
Hebei Special Vehicle Modification Technology Innovation Center,Hebei Vocational University of Technology and Engineering,Xingtai 054000,Hebei,China
Institute of Engineering Technology,University of Science and Technology Beijing,Beijing 100083,China
School of Petroleum and Natural Gas Engineering,Changzhou University,Changzhou 213164,Jiangsu,China
展开 >
Science and Technology Plan Foundation of Xingtai,ChinaJiangsu Key Laboratory of Oil-Gas Storage and Transportation TechnologyScience and Technology Project of Hebei Education Department
NETL
NSTL
万方数据