聚三亚甲级碳酸酯增韧聚乳酸的研究

Research of Toughening Poly(L-lactide)by Blending with Poly(trimethylene carbonate)

扫码查看
原文链接
  • 维普
  • 万方数据
为了提高左旋聚乳酸(PLLA)的韧性,通过溶液共沉淀法制备了不同质量比(100/0、95/5、90/10、85/15和80/20)的PLLA/PTMC二元复合材料.并以二者的无规共聚物(PLT)为增容剂,向PLLA/PTMC 90/10复合物中分别添加质量分数为1％、3％和5％的PLT,对该复合材料的热力学性质、内部结构和力学性能进行了研究.结果表明:PLT的加入可以提高PLLA和PTMC的相容性,与PLLA相比,复合材料的韧性明显提高.
To toughen poly(L-lactide)(PLLA),PLLA/PTMC 100/0,95/5,90/10,85/15,80/20(w/w)blends were prepared by solution coprecipitation.And PLLA/PTMC 90/10 blends with 1％,3％and 5％(mass fraction)poly(L-lactide-co-trimethylene carbonate)(PLT)as compatibilizer were also prepared by solution coprecipitation.The thermal,morphological,and mechanical of the compos-ite samples were studied in detail.The results indicated that the addition of PLT can increase the com-patibility of PLLA and PTMC,whose toughness was much improved compared with that of the neat PLLA.

PLLAPTMCcompatibilizerrandom copolymertoughen

谢旭龙、白威、罗智

展开 >

中国科学院成都有机化学研究所,四川成都 610041

中国科学院大学,北京 100039

四川省化工设计院,四川成都 610015

左旋聚乳酸 聚三亚甲基碳酸酯 无规共聚物 增容剂 增韧

国家自然科学基金资助项目

51103156

2024

10.15952/j.cnki.cjsc.1005-1511.23161

合成化学
四川省化学化工学会　中国科学院成都有机化学研究所

合成化学

CSTPCD
影响因子：0.42
ISSN：1005-1511
年,卷(期)：2024.32(9)