PLA/PPC/CS复合材料的制备工艺

扫码查看
原文链接
  • 万方数据
  • 维普
通过在聚乳酸(PLA)/玉米秸秆(CS)复合材料中引入聚碳酸亚丙酯(PPC)改善韧性,使用熔融挤出与热压成型相结合的方式制备聚乳酸/聚碳酸亚丙酯/玉米秸秆(PLA/PPC/CS)复合材料,以热压时间、热压压力和热压温度为变量,以PLA/PPC/CS复合材料的冲击、弯曲和拉伸性能为评价指标设计单因素试验.试验结果表明,热压时间、热压压力、热压温度对PLA/PPC/CS复合材料的力学性能影响显著.最终优化出的热压工艺条件为热压时间10 min,热压压力7.5 MPa,热压温度190 ℃.
Preparation process of PLA/PPC/CS composite materials
To improve the toughness of the PLA/corn stalk composite,the introduction of polypropylene carbonate(PPC)was used.The PLA/PPC/corn stalk(PLA/PPC/CS)composite was prepared using a combination of melt extrusion and hot pressing.A single factor experiment was designed with hot pressing time,hot pressing pressure,and hot pressing temperature as variables,and the impact,bending,and tensile properties of the PLA/PPC/CS composite as evaluation indicators.The results showed that the hot pressing time,hot pressing pressure,and hot pressing temperature had significant effects on the mechanical properties of PLA/PPC/CS composites.The final optimized hot pressing process is:hot pressing time is 10 min,hot pressing pressure is 7.5 MPa,and hot pressing temperature is 190 ℃.

wood-plastic composite materialspolylactic acidpolypropylene carbonatehot pressing processmechanical property

赵梓函、孟令宇、李祥瑞、李春风、刘明利

展开 >

北华大学材料科学与工程学院,吉林吉林 132013

吉林省林业科学研究院林业资源利用研究所,吉林长春 130117

木塑复合材料 聚乳酸 聚碳酸亚丙酯 热压工艺 力学性能

吉林省创新创业人才项目吉林省重点科技攻关项目吉林省重点科技攻关项目吉林省科技发展创新平台(基地)人才专项人才专项吉林省预算内基本建设资金(创新能力建设)项目

2023QN4420220202095NC20230202092NC20220508119RC20240601038RC2022C039-4

2024

10.3969/j.issn.1000-1565.2024.05.008

河北大学学报(自然科学版)
河北大学

河北大学学报(自然科学版)

CSTPCD北大核心
影响因子：0.322
ISSN：1000-1565
年,卷(期)：2024.44(5)
  • 7