首页|月桂酸基二元低共融储能材料的制备及热性能

月桂酸基二元低共融储能材料的制备及热性能

扫码查看
原文链接
  • 国家科技期刊平台
  • NETL
  • NSTL
  • 万方数据
相变材料的潜热储能技术利用于建筑节能领域.以月桂酸(LA)为基础,引入石蜡(PW)和癸酸(CA),研究月桂酸基二元相变材料的热性能、稳定性及可靠性.通过理论预测得到LA-PW、LA-CA的相变温度为35.75℃和18.11℃,通过实验得到LA-PW的最佳比例为76∶24,LA-CA的最佳比例为30∶70.LA-PW、LA-CA的相变温度分别为37.45℃和17.82℃,与理论值相差1.70℃、0.29℃,相变潜热分别为186.9J/g、129.16J/g.FTIR和XRD分析发现LA-PW、LA-CA都没产生新物质,为纯物理结合且在蓄放热实验过程中表现出良好的储热性能.热重分析可以看出在100℃内,LA-PW、LA-CA都没有发生热解现象,表现出良好的热可靠性.经过500次冷热循环后LA-PW、LA-CA的相变温度最大差率分别为9.5%、2.15%,相变潜热最大差率分别为3.8%、3.27%,能保持较好的稳定性和蓄热性能,适用于建筑行业的节能研究应用.
Preparation and thermal properties of lauric acid-based binary low compatible energy storage materials
The latent heat energy storage technology of phase change materials is utilized in the field of energy saving in buildings.Based on lauric acid(LA),paraffin wax(PW)and capric acid(CA)were introduced to investigate the thermal properties,stability and reliability of lauric acid-based binary phase change materials.The phase transition temperatures of LA-PW and LA-CA were obtained from theoretical predictions to be 35.75℃and 18.11℃,respectively.The optimal ratio of LA-PW was obtained experimentally as 76∶24 and the optimal ratio of LA-CA as 30∶70.The phase transition temperatures of LA-PW and LA-CA were 37.45℃and 17.82℃,respectively,which differed from the theoretical values by 1.70℃and 0.29℃,and the latent heats of phase transition were 186.9J/g and 129.16J/g,respectively.The FTIR and XRD showed that LA-PW and LA-CA did not produce any new material and were purely physically bonded withgood thermal storage performance during the heat storage and exothermic experiments.Thermogravimetric analysis showed that no pyrolysis occurred in LA-PW and LA-CA within 100℃,showing good thermal reliability of them.The maximum variation rates of phase change temperature of LA-PW and LA-CA during 500 cold and hot cycles were 9.5%and 2.15%respectively,and the maximum variation rates of latent heat of phase change were 3.8%and 3.27%respectively,demonstrating LA-PW and LA-CA hadgood stability and heat storage performance,and were suitable for energy-saving research applications in the building industry.

fatty acidscomposite phase change materialslatent heat energy storagethermal reliabilitybuilding energy efficiency

梁西妹、费华、李元林、雍帆、郭梦倩、周嘉宏

展开 >

江西理工大学土木与测绘工程学院,江西 赣州 341000

江西理工大学理学院,江西 赣州 341000

脂肪酸 复合相变材料 潜热储能 热可靠性 建筑节能

国家自然科学基金江西省自然科学基金江西省教育基金江西省教育基金江西理工大学清江青年优秀人才项目

5196600420212BAB204029GJJ2200841GJJ190447JXUSTQJYX2017003

2024

10.16085/j.issn.1000-6613.2023-0893

化工进展
中国化工学会,化学工业出版社

化工进展

CSTPCD北大核心
影响因子：1.062
ISSN：1000-6613
年,卷(期)：2024.43(6)
  • 36