新型超支化聚磷酰胺/聚磷酸铵协效阻燃聚丙烯的机理研究

扫码查看
原文链接
  • NETL
  • NSTL
  • 万方数据
  • 维普
以三聚氰胺(MEL)和二氯磷酸苯酯(PDCP)为主要原料,通过一步法(A2+B3)制备出一种含磷、氮、三嗪环及苯环结构的超支化聚磷酰胺(HBPPA)成炭剂,运用X射线光电子能谱(XPS)、核磁(1 H-NMR)对其化学结构进行了详细分析,并将其运用于阻燃聚磷酸铵(APP)/聚丙烯(PP)(APP/PP)复合材料.将25％(wt,质量分数)(APP∶HBPPA=3∶1)的膨胀型阻燃剂添加于PP时,制得的阻燃PP复合材料达到了UL-94的V0级别,极限氧指数达到30.6％.
Study on synergistic flame-retardant mechanism of novel hyperbranched polyphosphoramide and ammonium polyphosphate for polypropylene
A novel hyperbranched polyphosphoramide(HBPPA)charring agent,containing P and N elements as well as triazine and benzene rings,was successfully prepared by one-pot method(A2+B3)from melamine(MEL)and phenyl dichlorophosphate(PDCP).XPS and 1 H-NMR were used to analyze the chemical structure of HBPPA.With the addition of 25wt％(APP∶HBPPA=3∶1)of intumescent flame retardant,PP composite passed V0rating at UL-94test and its limiting oxygen index was increased to 30.6％.

hyperbranched polyphosphoramideammonium polyphosphatepolypropylene

叶新明、王远航、靳晴、晏泓

展开 >

太原理工大学新材料界面科学与工程教育部重点实验室,太原 030024

太原理工大学材料科学与工程学院,太原 030024

超支化聚磷酰胺 聚磷酸铵 聚丙烯

国家自然科学基金青年科学基金山西省自然科学基金

213061242015011035

2018

化工新型材料
中国化工信息中心

化工新型材料

CSCD北大核心
影响因子：0.357
ISSN：1006-3536
年,卷(期)：2018.46(5)
  • 6
  • 2