首页|焊接工艺参数对TA15/304不锈钢真空扩散焊接头组织与抗剪强度影响

焊接工艺参数对TA15/304不锈钢真空扩散焊接头组织与抗剪强度影响

扫码查看
原文链接
  • NETL
  • NSTL
  • 万方数据
针对TA15钛合金与 304不锈钢的异种金属连接及其接头进行了研究.结果表明,在 850～950℃的焊接温度下,接头扩散区(β-Ti区)和(α+β)-Ti双相区的宽度随温度的升高而增加,元素扩散更充分,接头孔洞逐渐减少,观察到逐渐增加的分层产物.分层产物主要为金属间化合物组成的界面层,即σ-Fe(第 1层),FeTi+Fe2Ti(第 2层),FeTi+β-Ti(第 3层)和β-Ti(第 4层).当焊接温度为 900℃时,焊接接头达到最大抗剪强度为 108 MPa,随着焊接时间的提升,焊接接头的微观形貌,元素成分和物相组织与焊接温度参数接头类似,但焊接时间对接头的抗剪强度影响较小,当焊接时间为 80 min时,抗剪强度达到最大,断口出现以韧性为主的脆-韧性混合断裂特征.
Influence of welding process parameters on the microstructure and shear strength of TA15/304SS vacuum diffusion welded joints
A study was conducted on the dissimilar metal connection and joint between TA15 titanium alloy and 304 stainless steel.The experimental results show that at welding temperatures of 850-950℃,the diffusion zone of the joint(β-Ti)District and(α+β)Ti biphasic region increases with the increase of temperature,element diffusion is more complete,joint pores gradually decrease,and an increasing number of layered products are observed.The layered products are mainly interface layers composed of intermetallic compounds,namely σ-Fe(1st layer),FeTi+Fe2Ti(2nd layer),FeTi+β-Ti(3rd layer)and β-Ti(4th layer).When the welding temperature is 900℃,the welded joint reaches its maximum shear strength of 108MPa.As the welding time increases,the microstructure and composition of the welded joint are similar to those of the welding temperature parameter joint,but the influence of welding time on the shear strength of the joint is relatively small.When the welding time is 80 minutes,the shear strength reaches its maximum value,and the fracture surface exhibits a brittle ductile mixed fracture feature dominated by toughness.

TA15/304SSwelding of dissimilar metalsvacuum diffusion weldingprocess parametersmicroscpic organizationmechanical property

余曦、李琪、常荣辉、秦彬皓、张宇鹏、尹立孟、王海燕

展开 >

广东省科学院中乌焊接研究所,广东省现代焊接技术重点实验室,广州,510650

重庆科技大学,冶金与材料工程学院,重庆,401331

沈阳飞机工业(集团)有限公司,沈阳,110034

TA15/304SS 异种金属焊接 真空扩散焊接 工艺参数 微观组织 力学性能

国家重点研发计划广东省科技计划广东省科学院发展专项广东省科学院发展专项广东省科学院发展专项

2020YFE02053002022B12120500012020GDASYL-202003010012022GDASZH-20220101092022GDASZH-2022010203

2024

10.12073/j.hjxb.20230630001

焊接学报
中国机械工程学会　中国机械工程学会焊接学会　机械科学研究院哈尔滨焊接研究所

焊接学报

CSTPCD北大核心
影响因子：0.815
ISSN：0253-360X
年,卷(期)：2024.45(5)
  • 10