脉冲电流对电化学除氯的影响
Effect of Pulse Current on Electrochemical Dechlorination
李冬韵 1孙玉朋 1王长罡 2陈昊男 2唐军务 3历峰 4赵楠 5郭泉忠 2赵茹3
作者信息
- 1. 中国科学院金属研究所,沈阳 110000;中国科技大学 材料科学与工程学院,沈阳 110000
- 2. 中国科学院金属研究所,沈阳 110000
- 3. 海军勤务学院,天津 300000
- 4. 中铁三局集团电务工程有限公司,天津 300000
- 5. 北京市昌平区河湖生态环境服务中心,北京 102200
- 折叠
摘要
目的 探究不同电流密度下,直流和脉冲2种电流模式对钢筋混凝土电化学除氯的影响,降低钢筋渗氢量,减小通电后阴极产生的氢气使钢筋发生氢脆的风险,提高除氯效率,改善电化学除氯效率的均匀性.方法 通过在电流密度为2、3、4 A/m2 的条件下,对混凝土进行直流和脉冲电流电化学修复,测定处理后的钢筋的释氢电流,计算释氢总电量,来表示钢筋渗氢量,对比处理后强电流区和弱电流区混凝土的氯离子含量,分析 2 种方式除氯效率的均匀性,同时用扫描电子显微镜观察电化学除氯前后混凝土的微观结构.结果 计算得到不同通电电流密度下钢筋的释氢总电量和除氯效率,脉冲电流的释氢总电量比直流电流低约20%,而除氯效率提高了约 10%.结论 增加电流密度可以提高除氯效率,但是会增加钢筋发生氢脆的风险.相较于直流电流,脉冲电流电化学修复可以降低钢筋渗氢量,显著提高弱电流区的除氯效率,从而改善除氯效率的均匀性.
Abstract
The work aims to explore the influence of direct current and pulse current on the electrochemical dechlorination of reinforced concrete at different current densities,reduce the hydrogen permeation amount and hydrogen embrittlement risks of steel bars,so as to improve the efficiency of dechlorination and the uniformity of electrochemical dechlorination efficiency.The current densities of 2,3 and 4A/m2 were selected,and the concrete was electrochemically repaired by direct current and pulse current.The hydrogen release current of the treated steel bar was measured,and the total hydrogen release electricity was calculated to represent the hydrogen permeation amount of the steel bar.The chloride ion content of concrete in the solid current area and weak current area after treatment was compared,and the uniformity of dechlorination efficiency of the two methods was analyzed.At the same time,the microstructure of concrete before and after electrochemical dechlorination was observed by scanning electron microscope.The total hydrogen release amount and chlorine removal efficiency of steel bars with different current densities were calculated.Compared with direct current,the total amount of hydrogen released with pulse current is re-duced about 20%,while the chlorine removal efficiency is improved about 10%.The results show that increasing the current density can improve the dechlorination efficiency but increase the risk of hydrogen embrittlement of steel bars.Compared with direct current,the hydrogen permeation of the steel bar is reduced by electrochemical repair with a pulse current,and the dechlorination efficiency in the weak current region is significantly improved.Thus,the uniformity of dechlorination efficiency is improved.
关键词
脉冲电流/电化学除氯/氢脆/电流密度/混凝土/腐蚀Key words
pulse current/electrochemical chloride removal/hydrogen embrittlement/current density/concrete/corrosion引用本文复制引用