Hot Compression Behavior and Tensile Property of a Novel Ni-Co-Based Superalloy Prepared by Electron Beam Smelting Layered Solidification Technology
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
万方数据
维普
The hot compression behavior and tensile strength after compression of a new Ni-Co-based superalloy produced using elec-tron beam smelting layered(EBSL)solidification technology were investigated.Isothermal compression tests were performed at temperatures of 1120 ℃ and 1150 ℃,with strain rates of 1 s-1 and 0.01 s-1,reaching a true strain of 0.51.Tensile strength was evaluated at room temperature.The results revealed that this EBSL technology accelerates dynamic recrystallization(DRX),without compromising the strength of alloy.A significant correlation between the volume fraction of DRX and the strain rate was observed,with higher fractions at lower strain rates,leading to higher tensile strength.Additionally,at the same strain rate,the specimens compressed at 1120 ℃ exhibited higher tensile strength due to undissolved γ'precipitates.After solution and aging heat treatment,the alloy maintained high tensile strength.The results suggested that the EBSL Ni-Co-based superalloy offers excellent prospects for practical applications.
Yong-Chao Gai、Rui Zhang、Chuan-Yong Cui、Zi-Jian Zhou、Yi Tan、Yi-Zhou Zhou、Xiao-Feng Sun
展开 >
Key Laboratory of Materials Modification by Laser,Ion,and Electron Beams(Ministry of Education),School of Materials Science and Engineering,Dalian University of Technology,Dalian 116024,China
Shi-Changxu Innovation Center for Advanced Materials,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China
国家重点研发计划国家科技重大专项中国科学院青年创新促进会项目Natural Science Foundation Project of Liaoning Province
万方数据
维普