水溶性氧化钙陶瓷型芯的挤出式3D打印参数优化与表面精度控制研究

扫码查看

原文链接

万方数据
维普

中文摘要：挤出式3D打印成形水溶性氧化钙陶瓷型芯可高质高效成形复杂内腔铸造构件,铸件内腔的残留型芯用水溶解即可快速清理,在复杂内腔构件精密铸造领域具有较大的应用潜力.以针头内径、层高/内径比值、打印速度和内部填充方向四个关键工艺参数进行四因素三水平正交试验,通过对不同工艺参数的3D打印成型坯体进行表面粗糙度测量与统计,采用极差分析确定各个打印参数对坯体表面质量影响的主次顺序,并得到挤出式3D打印氧化钙陶瓷型芯的最优打印参数.结果表明,内部填充方向对型芯坯体表面成形质量有显著的影响,当内部填充方向与外轮廓呈45°和90°时,内部填充浆料与外轮廓层有较多的拐点,拐点处的成形方向发生突变,进而造成挤出压力方向发生突变并作用于外轮廓层,外轮廓层变得凹凸不平,层层堆积成形的坯体表面粗糙度较大、表面质量较差.当针头内径为0.41mm、层高/内径比值为70％、打印速度为20mm/s、内部填充方向与外轮廓层平行时,坯体表面粗糙度最小,型芯坯体表面质量最好.通过增加外轮廓层数来可以有效地减小甚至消除填充方向对坯体表面粗糙度的影响,当外轮廓增加至两层时型芯坯体表面粗糙度降低了近22％,这对水溶性陶瓷型芯的快速精确成形具有重要意义.

外文标题：Parameter Optimization and Surface Accuracy Control of Water Soluble Calcia Ceramic Core Prepared by Extrusion 3D Printing Technology

外文摘要：Water-soluble calcia ceramic core prepared by extrusion 3D printing technology is used to form complex internal cavity casting components with high quality and efficiency,and the residual cores after casting are quickly removed by dissolving with water,which possesses a large potential for application in precision casting of complex internal cavity components.A four-factor,three-level orthogonal experiment is conducted with four key process parameters:needle diameter,layer height/needle diameter ratio,printing speed,and internal filling direction.By measuring and counting the surface roughness of 3D printed forming green bodies with different process parameters,the influences of each printing parameter on the surface quality of the printed green bodies are determined using extreme difference analysis,and the optimal printing parameters for extrusion 3D printing of calcia ceramic cores were obtained.The results show that the internal filling direction has a significant effect on the surface-forming quality of the green bodies.When the internal filling direction is 45 ° and 90 ° to the outer contour,there are many inflection points between the internal filling slurry and the outer contour layer,and the forming direction at the inflection point changes suddenly,resulting in sudden changes in the direction of the extrusion pressure and acting on the outer contour layer,the outer contour layer becomes uneven,and the surface roughness of the green body formed layer by layer by layer is large poor surface quality.When the needle inner diameter is 0.41 mm,the layer height/needle diameter ratio is 70％,the printing speed is 20 mm/s,and the internal filling direction is parallel to the outer contour layer,the surface roughness of the green body is the minimum,and the surface quality of the core green body is the best.By increasing the number of layers of the outer profile,the influence of the filling direction on the surface roughness of the blank can be effectively reduced or even eliminated,when the outer profile is increased to two layers,the surface roughness of the core blank is reduced by about 22％,which is important for the rapid and accurate forming of water-soluble ceramic cores.

外文关键词：

calcia ceramic coresextrusion 3D Printinginternal filling directionnumber of outer profile layers

作者：

穆英朋、刘富初、张驰、黄捷飞、刘鑫、韩光超、樊自田、许峰

展开 >

作者单位：

中国地质大学(武汉)机械与电子信息学院武汉 430074

中国地质大学深圳研究院深圳 518057

华中科技大学材料成形与模具技术国家重点实验室武汉 430074

荆门市炬峰机械设备制造有限公司荆门 448000

展开 >

关键词：

氧化钙陶瓷型芯挤出式3D打印内部填充方向外轮廓层数

基金：

中央引导地方科技发展资金自由探索类基础研究中央引导地方科技发展资金自由探索类基础研究材料成形与模具技术国家重点实验室开放课题研究基金中央高校基本科研业务费专项国家自然科学基金湖北省揭榜制科技湖北省支持企业技术创新发展(高新技术企业类)中国地质大学(武汉)教学实验室开放基金中国地质大学(武汉)教学实验室开放基金中国地质大学(武汉)教学实验室开放基金中国地质大学(武汉)教学实验室开放基金大学生创新创业训练计划大学生创新创业训练计划大学生创新创业训练计划大学生创新创业训练计划

项目编号：

2021Szvup1582021Szvup159P20121-020CUG2106346517752042021BEC0102021BAB050SKJ2021113SKJ2021131SKJ2022119SKJ2022136202210491005S202210491083X202210491025X202210491029

出版年：

2024

DOI：

10.3901/JME.2024.01.170

机械工程学报

中国机械工程学会

机械工程学报

CSTPCD北大核心

影响因子：1.362

ISSN：0577-6686

年,卷(期)：2024.60(1)

参考文献量23