通过分析砂浆的外观、质量损失率和耐蚀系数,结合X射线衍射(XRD)、扫描电镜(SEM)和元素能谱分析(EDS)等微观测试手段,对比研究了硅酸盐水泥、铝酸盐水泥浆体在硫酸、柠檬酸溶液中的腐蚀规律与机理.结果表明:与硫酸溶液相比,柠檬酸溶液对两种水泥砂浆的腐蚀能力更强;与硅酸盐水泥相比,铝酸盐水泥表现出了较好的耐酸腐蚀性能,主要原因在于铝酸盐水泥硬化浆体中含有大量铝胶,在硫酸溶液中能够中和更多H+,在柠檬酸溶液中能够延缓H+向硬化浆体内部扩散的速率.
Corrosion and Mechanism of Sulfuric Acid and Citric Acid Solution on Cement Hardened Paste
The corrosion laws and the mechanisms of Portland cement hardened paste and aluminate cement hardened paste in sulfuric acid and citric acid solutions were studied by analyzing the appearance change of mortar,measuring the mass loss rate and corrosion resistance coefficient of mortar in acid solutions combined with X-ray diffraction(XRD),scanning electron microscopy(SEM)and elemental energy spectroscopy(EDS).The results show that compared with sulfuric acid solution,citric acid solution has stronger corrosion ability for two cement mortars.Compared with Portland cement,aluminate cement shows better acid corrosion resistance,mainly because the hardened paste of aluminate cement contains a large amount of aluminum glue,which can neutralize more H+ in sulfuric acid solution and delay the diffusion rate of H+ to the inside of the hardened paste in citric acid solution.

acid corrosioncitric acidsulfuric acidaluminate cementPortland cement

金惠玲、孙振平、杨海静、马跃飞、李志林

展开 >

同济大学 先进土木工程材料教育部重点实验室,上海 201804

同济大学 材料科学与工程学院,上海 201804

上海市水务局城市管网智能评估与修复工程技术研究中心,上海 201900

乌兰浩特市圣益商砼有限公司,内蒙古 乌兰浩特 137400

云南氟业环保科技股份有限公司,云南 昆明 650011

展开 >

酸腐蚀 柠檬酸 硫酸 铝酸盐水泥 硅酸盐水泥

国家自然科学基金国家自然科学基金上海市科委项目上海市科委项目上海市建委专项上海市科委-上海市外专局项目重庆市科技局专项内蒙古自治区科技计划云南省科技厅专家工作站项目

522782725210824019DZ120270219DZ1201404住建管2021-001-00222WZ2502400cstc2020kqjscxphxm15942022YFDZ0063202105AF150243

2024

10.3969/j.issn.1007-9629.2024.01.008

建筑材料学报
同济大学

建筑材料学报

CSTPCD北大核心
影响因子：1.046
ISSN：1007-9629
年,卷(期)：2024.27(1)
  • 7