Low Temperature Sulfuric Acid Ripening-water Leaching for Vanadium Extraction from Stone Coal Vanadium Ore
曹欢 1靳建平 1赵笑益 1梁效 1宁新霞1
作者信息
- 1. 西安西北有色地质研究院有限公司,陕西省矿产资源综合利用工程技术研究中心,陕西 西安 710054
- 折叠
摘要
这是一篇冶金工程领域的论文.以陕西某地含钒矿物为绢云母、伊利石的石煤钒矿为研究对象,采用低温硫酸熟化-水浸工艺提钒,考查了熟化温度、熟化时间、硫酸用量、氯化钠用量,浸出温度、浸出时间及浸出液固比对钒浸出率的影响.结果表明:向石煤钒矿中加入25％的硫酸、0.8％的氯化钠,在130 ℃下熟化8h,熟化样品在浸出温度55 ℃、液固比1.5∶1的条件下浸出时间2h,钒浸出率可达89％.这说明采用低温(130℃)硫酸熟化-水浸工艺提取石煤型钒矿是可行的.
Abstract
This is an article in the field of metallurgical engineering.The vanadium ore with vanadium containing sericite and illite in Shaanxi province was taken as the research object,low-temperature sulfuric acid ripening-water leaching process was used to extract vanadium.The effects of ripening temperature,ripening time,sulfuric acid dosage,sodium chloride dosage,leaching temperature,leaching time and liquid-solid ratio on vanadium leaching rate were investigated.The results show when 25％sulfuric acid and 0.8％sodium chloride are added to the stone coal vanadium ore,the sample is aged at 130 ℃ for 8 h,and the sample is leached at 55 ℃ for 2 h under the conditions of liquid-solid ratio of 1.5∶1,the vanadium leaching rate can reach more than 89％.This indicates that it is feasible to adopt low temperature sulfuric acid ripening and water leaching process to extract stone coal type vanadium ore.
关键词
冶金工程/石煤钒矿/硫酸熟化/提钒/水浸Key words
Metallurgical engineering/Stone coal vanadium ore/Sulfuric acid ripening/Extracting vanadium/Water leaching引用本文复制引用