ZT基轻质镁合金材料显微硬度测试及规律分析

Microhardness Test and Law Analysis of ZT Base Light Magnesium Alloy Materials

许东光 ¹孙浩浩 ¹仲志国 ²马春华²

扫码查看

作者信息

1. 南阳师范学院智能制造与电气工程学院,河南南阳 473061
2. 南阳师范学院智能制造与电气工程学院,河南南阳 473061;河南省稀土合金材料工程技术研究中心,河南南阳 473061
折叠

摘要

以Mg-6Zn-3Sn-xCa,x=(0、0.3、0.6、1.0,1.5)合金为研究对象,制作出5组试样后进行金相处理.用HXS-1000AY数字式显微硬度仪进行维氏硬度测试,用HD-AP硬度进行显微组织图像和硬度数据的收集.Ca含量的镁合金为0％、0.3％、0.6％时硬度较为稳定,当Ca含随着Ca含量从0％到达1.0％,镁合金硬度提高47.35％,硬度提升到65HV以上,之后硬度值会有所下降.当Ca含量从0％到1.5％时,通过显微组织观察合金中的第二相Mg2Ca大量析出细化了结晶组织提升镁合金硬度.

Abstract

In this paper,Mg-6Zn-3Xn-xCa(0,0.3,0.6,1.0,1.5)alloy was taken as the research object,and five groups of samples were fabricated and then metallographic treated.Vickers hardness was measured by HXS-1000AY digital microhardness tester,and microstructure images and hardness data were collected by HD-AP hard-ness.The hardness of magnesium alloy with 0％,0.3％and 0.6％Ca content is relatively stable.When Ca content increases from 0％to 1.0％,thehardness of magnesium alloy increases by 47.35％to over 65HV,and then the hardness value decreases.When the content of Ca is from 0％to 1.5％,the second phase Mg2Ca in the alloy is precipitated to refine the crystal structure and improve the hardness of magnesium alloy.

关键词

Mg-6Zn-3Sn-xCa合金/金相制备/显微组织/硬度测试分析

Key words

Mg-6Zn-3Sn-xCa alloy/Metallographic preparation/Microstructure/Hardness test and Analysis

引用本文复制引用

基金项目

河南科技厅科技攻关项目(212102210437)

南阳市2022年基础与前沿技术研究计划项目(JCQY003)

2023年度南阳师范学院理工科校级STP项目(2023STP004)

出版年

2024

绿色科技

花木盆景杂志社

绿色科技

影响因子：0.365

ISSN：1674-9944

参考文献量21

段落导航