固溶处理对电弧增材制造超级双相不锈钢微观组织及摩擦磨损性能的影响

扫码查看

原文链接

NETL
NSTL
万方数据

中文摘要：采用直径为1.2 mm的ER2594-超级双相不锈钢焊丝进行了多层单道墙体电弧增材试验,对增材件分别进行1 050、1 150和1 250℃的固溶处理,并在固溶处理后对各试样进行了往复式摩擦磨损试验.试验结果表明:随着固溶温度的升高,双相比中的铁素体含量增加,其显微硬度也相应提高.此外,固溶处理可降低增材件的内应力,最终基于较高硬度和较低内应力的协同作用,在1 250℃时获得耐磨性能较优的试样,有效地提升了热处理后增材件试样的摩擦磨损性能.

外文标题：Effect of Solution Treatment on Microstructure and Wear Resistance of Directed Energy Deposited Super Duplex Stainless Steel

外文摘要：A multi-layer single-pass wall deposition experiment was conducted using ER2594 super duplex stainless steel welding wire with a diameter of 1.2 mm.The additively manufactured specimens were subjected to solution treatment at temperatures of 1 050,1 150 and 1 250℃,followed by reciprocating friction and wear tests.The experimental results revealed that with the increase in solution treatment temperature,the ferrite content in the duplex phase increased,leading to a corresponding increase in microhardness.Furthermore,the solution treatment effectively reduced the internal stresses in the additively manufactured components.Ultimately,based on the synergistic effect of higher hardness and lower internal stresses,the specimen treated at 1 250℃exhibited superior wear resistance in the friction and wear tests.The wear resistance of the samples after heat treatment were effectively improved.In summary,the findings of this study highlighted the importance of solution treatment temperature in determining the microstructural and mechanical properties of additively manufactured super duplex stainless steel components.By optimizing the solution treatment conditions,it was possible to improve the wear resistance of these components,thereby enhancing their overall performance in various applications.

外文关键词：

super duplex stainless steeladditive manufacturingsolution treatmentinternal stresswear

作者：

李科、林义民、王飞、易江龙、邹晓东、潘琳琳、牛犇

展开 >

作者单位：

五邑大学智能制造学部,广东江门 529030

广东省科学院中乌焊接研究所广东省现代焊接技术重点实验室,广东广州 510651

宝武特种冶金有限公司技术中心,上海 200940

关键词：

超级双相不锈钢增材制造固溶处理内应力摩擦磨损

基金：

广州市基础与应用基础研究项目广东省省级科技计划项目广东省基础与应用基础研究基金项目广东省科学院建设国内一流研究机构行动专项资金广州市科技计划项目

项目编号：

2022010110772022A05050500522021A15150117562021GDASYL-20210103083201604046026

出版年：

2024

DOI：

10.16078/j.tribology.2023130

摩擦学学报

中国科学院兰州化学物理研究所

摩擦学学报

CSTPCD北大核心

影响因子：0.815

ISSN：1004-0595

年,卷(期)：2024.44(7)