镀铜刨花人造板的制备及其力学性能探究
THE PREPARATION AND THE STUDY OF MECHANICS PROPERTIES OF THE COPPER PLATING AT MAN-MADE BOARD
胡士伟 1崔魏月 2沈源 黄金田1
作者信息
- 1. 内蒙古农业大学材料科学与艺术设计学院,呼和浩特010018
- 2. 内蒙古森工集团,牙克石022150
- 折叠
摘要
以杨木刨花作为基材,对在杨木刨花表面金属化处理以后进行化学镀铜,研究了施胶量、热压温度和密度对镀铜刨花人造板力学性能的影响.试验结果表明:在施胶量为12％、热压温度为80℃、板材密度为1.0 g/cm3的工艺条件下生产的人造板具有良好的力学性能,此时板材的弹性模量为2992MPa,静曲强度为43MPa,24h吸水厚度膨胀率为4.9％.
Abstract
We found that used cotton wood shavings as substrate,on the surface of metal particles in the company before treatment chemical plating copper.The mechanics properties of glue quantity and hot-pressing temperature and density on copper shavings wood -based panels were research.The results showed that:when the rate of spreading was 12％ and the hot-pressing temperature was 80℃ and the density was 1.0 g/cm3,the man-made board has good mechanical properties.and in those condition the elastic modulus of the elasticity was 2992MPa、the bending strength was 43MPa and the thickness swelling after 24 hours was 4.9％.
关键词
化学镀铜/工艺/力学性能Key words
Treatment chemical plating copper/process/mechanics properties引用本文复制引用