燃煤锅炉水冷壁高温腐蚀形成原因及防治措施

扫码查看
近年来,电厂为降低成本大量掺烧经济煤种,导致锅炉水冷壁高温腐蚀问题日趋严重,随着锅炉机组参数不断提高,部分机组出现了严重腐蚀,加大了治理的困难.时而发生的停机事故严重影响了锅炉的安全稳定运行,频繁的停机检修与建材更换造成了各电厂的严重经济损失,迫切需要研究切实可行的锅炉水冷壁高温腐蚀防治措施.本文系统分析了锅炉水冷壁严重高温腐蚀形成的原因及影响因素,并总结了一些当前较为先进的锅炉水冷壁高温腐蚀的防治措施及其存在的问题,以期为各电厂解决锅炉水冷壁高温腐蚀问题提供技术思路.
Reasons and Prevention Measures for High-temperature Corrosion of Water-cooled Walls in Coal-fired Boilers
In recent years,due to the extensive blending of economic coal in power plants,the problem of high-temperature corrosion of boiler water-cooled walls has become increasingly serious.With the continuous improvement of boiler unit parameters,some units have experienced severe corrosion,increasing the difficulty of treatment.The frequent shutdown accidents seriously affect the safe and stable operation of boilers,and frequent shutdown maintenance and building material replacement have caused serious economic losses to various power plants.It is urgent to study practical and feasible measures for preventing high-temperature corrosion of boiler water-cooled walls.This article systematically analyzes the causes and influencing factors of severe high-temperature corrosion of boiler water-cooled walls,and summarizes the current advanced prevention and control measures for high-temperature corrosion of boiler water-cooled walls,in order to provide technical ideas for various power plants to solve the problem of high-temperature corrosion of boiler water-cooled walls.

boilerwater cooled wallhigh temperature corrosionprevention and control

谈金军、丁鹏、吕馥丞、王有林、孔令军、曹发扬、付亚杰、金立梅

展开 >

华电青岛发电有限公司,山东 青岛 266031

西安格瑞电力科技有限公司,陕西 西安 710049

锅炉 水冷壁 高温腐蚀 防治

2024

全面腐蚀控制
中国工业防腐蚀技术协会

全面腐蚀控制

影响因子:0.278
ISSN:1008-7818
年,卷(期):2024.38(10)