高质量大尺寸氟化钙晶体是深紫外光刻、空天相机等高端应用不可或缺的光学材料，同时制备高质量大尺寸晶体也是晶体生长领域的难题。本文以数值手段分别模拟了 3、7和20英寸(1英寸=2。54 cm)氟化钙晶体在不同生长阶段的传热、流动及相变过程。结果表明，晶体尺寸增加大幅加强熔体流动强度，而且造成坩埚外壁散热部分的面积急剧增加，由此引发固液界面局部凹陷、径向温差增大、晶体边缘-中心温差翻转、生长界面附近的轴向温梯大幅衰减等问题。此外，本文还就大尺寸氟化钙晶体生长中的坩埚下降速率和发热体功率的优化控制策略进行了探讨。
Numerical Simulation Investigation of Size Effect on Calcium Fluoride Crystals Grown by Vertical Bridgman Method
High-quality,large-size CaF2 crystals are urgently needed for advanced applications such as deep ultraviolet lithography and aerospace cameras.However,growing such crystals is a challenging task in the field of crystal growth.Heat transfer,flow,and phase change processes of 3,7,and 20 inch(1 inch=2.54 cm)CaF2 crystals at different growth stages on the vertical Bridgman growth were conducted by numerical simulation.The results show that as the crystal size increases,the melt flow strength and the area of heat dissipation on the crucible wall increase,resulting in problems such as local depression of the melt-crystal interface,increase in the radial temperature difference,reversal of the temperature difference between the crystal edge and center,and decrease in the axial temperature gradient near the melt-crystal interface.Furthermore,this article discusses optimization strategies for growth rate and power of heater in the growth of large-size CaF2 crystals.

CaF2 crystalvertical Bridgman methodsize effectnumerical simulationmelt-crystal interfacetemperature gradient

施宇峰、王鹏飞、穆宏赫、苏良碧

展开 >

中国科学院上海硅酸盐研究所,上海 201899

中国科学院大学材料科学与光电工程中心,北京 100049

CaF2晶体 坩埚下降法 尺寸效应 数值模拟 固液界面 温度梯度

国家重点研发计划国家自然科学基金上海市科委项目上海市科委项目中国科学院稳定支持基础研究领域青年团队计划

2021YFE0104800619255082351110270023YF1413400YSBR-024

2024

人工晶体学报
中材人工晶体研究院

人工晶体学报

CSTPCD北大核心
影响因子：0.554
ISSN：1000-985X
年,卷(期)：2024.53(6)
  • 30