首页|刃具钢板探伤缺陷分析及改善措施

刃具钢板探伤缺陷分析及改善措施

扫码查看
针对HE46刃具钢板出现的探伤不合格问题,通过钢坯冷酸蚀检验、金相检验和截面成分波动测定,分析了裂纹缺陷的发生机理,确定了严重的中心偏析导致形成马氏体组织,在马氏体处形成裂纹,导致钢板探伤不合.通过调整电磁搅拌参数,调整热装生产方式,并辅助真空处理和带温切割和堆垛工艺,解决了钢板偏析导致的钢板探伤不合格问题.
Flaw Defection Analysis and Improvement Measures of Cutting Tool Steel Plat
According to the defect detection problem of HE46 cutting tool steel plate,the mechanism of crack defects was analyzed through billet cold acid corrosion test,metallographical observation and composition variation measurement in cross-section.It was determined that serious center segregation led to the formation of martensitic structure,and cracks formed in martensitic,leading to the failure detection of steel plate.By adjusting the electromagnetic stirring parameters,adjusting the hot charge production mode,and assisting vacuum treatment and temperature cutting and stacking technology,the problem of unqualified steel plate inspection caused by steel plate segregation is solved.

cutting tool steelcenter segregationmartensiticcrackelectromagnetic stirring

欧阳宇、马鑫、于浩、甄新刚、刘振华

展开 >

日钢营口中板有限公司,辽宁营口 115005

辽宁省中厚板专业技术创新中心,辽宁营口 115005

刃具钢 中心偏析 马氏体 裂纹 电磁搅拌