首页|小方坯生产冷镦钢的可浇性改善实践

小方坯生产冷镦钢的可浇性改善实践

扫码查看
某钢企一炼钢厂小方坯连铸机生产冷镦钢过程中,出现钢液可浇性差的问题,具体表现为塞棒上涨、结晶器液面波动等.在连铸工序,对含铝冷镦钢的水口堵塞情况进行了分析,并依据分析结果查找出聚集物来源主要为Al2O3及CaS.针对此提出了解决方案并予以实施,有效减少了因水口堵塞造成的质量波动及生产事故的发生.
Practice of Improving the Castability of Cold Heading Steel Produced From Small Billets
During the production of cold heading steel by a small billet continuous casting machine in a steel plant of a certain steel enterprise,there was a problem with the castability of the molten steel,which was manifested by the rise of the plug rod and the fluctuation of the crystallizer liquid level.In the continuous casting process,an analysis was conducted on the blockage of the water nozzle in aluminum containing cold heading steel,and based on the analysis results,it was found that the main sources of aggregates were Al2O3 and CaS.A solution has been proposed to effectively reduce quality fluctuations and production accidents caused by clogged water outlets.

small billetwaterabilitycold heading steelwater outlet blockage

杨森

展开 >

邯钢集团炼钢厂,河北 邯郸 056015

小方坯 可浇性 冷镦钢 水口堵塞

2024

山西冶金
山西省金属学会 山西省有色金属学会

山西冶金

影响因子:0.139
ISSN:1672-1152
年,卷(期):2024.47(9)