首页|Static and Fatigue Behavior of Hybrid Bonded/Bolted Glass Fiber Reinforced Polymer Joints Under Tensile Loading
Static and Fatigue Behavior of Hybrid Bonded/Bolted Glass Fiber Reinforced Polymer Joints Under Tensile Loading
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
万方数据
维普
This paper presents the static and fatigue tests of hybrid(bonded/bolted)glass fiber reinforced poly-mer(GFRP)joints.Nine specimens of single-lap hybrid GFRP joints have been fabricated to study the static and fatigue behaviors in the experimental campaign.The static tests of uniaxial tension loading are first conducted,from which the static ultimate bearing capacities of the joints are obtained.High-cycle fatigue tests are subse-quently carried out so that the fatigue failure mode,fatigue life,and stiffness degradation of joints can be obtained.The measuring techniques including acoustic emission monitoring and three-dimensional digital image correlation have been employed in the tests to record the damage development process.The results revealed that the static strength and fatigue behavior of such thick hybrid GFRP joints were controlled by the bolted connections.The four stages of fatigue failure process are obtained from tests and acoustic emission signals analysis:cumulative damage of adhesive layer,damage of the adhesive layer,cumulative damage of GFRP plate,and damage of GFRP plate.The fatigue life and stiffness degradation can be improved by more bolts.The S-N(fatigue stress versus life)curves for the fatigue design of the single-lap hybrid GFRP joints under uniaxial tension loading are also proposed.
万方数据
维普