Study on Waterborne 2K Primer-Topcoat Integrated Anticorrosive Coating
A kind of waterborne 2K primer-topcoat integrated anticorrosive coating system with good corrosion resistance and weatherability was described.The preparation process was described and the effects of the waterborne hydroxypropyl resin,isocyanate curing agent,anti-rust pigment,pigment to binder ratio(P/B)and the coating film thickness on the film appearance and other properties of the waterborne 2K anticorrosive coatings were analyzed.Thus,the"1C1B"coating process was obtained,wherein the single coating film thickness less than 45 μm could enable the salt spray resistance up to 360 h and the xenon lamp aging resistance up to 600 h.