Zn-9.5Al-3Mg-0.01Ce合金微观组织演化的研究
Microstructure Evolution of Zn-9.5Al-3Mg-0.01Ce Alloy
李积鹏 1谯德高 1罗晓阳 1董世文 1彭鹏 2闫显涛 2陈翠1
作者信息
- 1. 甘肃酒钢集团宏兴钢铁有限公司,嘉峪关 735100
- 2. 兰州大学材料与能源学院,兰州 730000
- 折叠
摘要
利用X射线衍射、扫描电镜和能谱仪对Zn-9.5Al-3Mg-0.01Ce合金的微观组织和相组成进行了研究.结果发现,炉冷条件下,该合金由初生Al枝晶,Al+MgZn2二元共晶,Al+Zn+Mg2Zn11三元共晶构成,初生Al枝晶不是单相.Al枝晶的边缘区域存在明显的台阶状形貌.结合线扫描结果可知,枝晶中心区域的Al含量比枝晶边缘部分高得多,而Zn含量则低得多.这是由于合金在凝固时发生了包晶反应.
Abstract
The microstructure and phase composition of Zn-9.5Al-3Mg-0.01Ce alloy were investigated by XRD,SEM and EDS.The results reveal that Zn-9.5Al-3Mg-0.01Ce alloy is composed of primary Al dendrites,Al+ MgZn2 binary eutectic,Al+Zn+Mg2Zn11 ternary eutectic under cold furnace conditions.The primary Al dendrites are non-single phase,and an obvious step-like morphology is observed at the edges of primary Al dendrites.EDS linear scan results indicate that the Al content at the inner of the dendrites are much higher than that at the external,while Zn content is the contrary,which is attributed to the peritectic reaction during solidification.
关键词
Zn-Al-Mg合金/微观组织/包晶反应Key words
Zn-Al-Mg Alloy/Microstructure/Peritectic Reaction引用本文复制引用
基金项目
甘肃省科技重大专项计划资助项目(22ZD6G13019)
甘肃省重点研发计划资助项目(23YF6A0003)
甘肃省联合科研基金重大资助项目(23JRRC0004)
凝固技术国家重点实验室开放课题资助项目(SKLSP202204)
中央高校基本科研业务费资助项目(1zujbky-2022-ey15)
出版年
2024
NETL
NSTL
维普
万方数据