Ti-6Al-4V钛合金凝固组织的CAFE法模拟
Solidification Microstructure Simulation of Ti-6Al-4V Alloy by CAFE Method
崔新鹏 1李峰 1马静 1张强1
作者信息
- 1. 中国航发北京航空材料研究院,北京市先进钛合金精密成型工程技术研究中心,北京 100095
- 折叠
摘要
利用ProCAST软件的CAFE模块模拟了Ti-6Al-4V合金的凝固晶粒组织,并采用精密铸造工艺制备阶梯试样来验证和评价模拟结果.模拟发现铸件表面晶粒呈柱状晶,到铸件心部转化成等轴晶,平均晶粒直径随着壁厚增加而增大,晶粒分布形态与试验结果一致.平均晶粒直径模拟结果与实际吻合率达80%～99%,符合工程应用预期.
Abstract
The CAFE module in ProCAST software was utilized to simulate the solidification grain structure of Ti-6Al-4V alloy,and the step specimen was prepared by investment casting to verify and evaluate the simulation results.The simulation results indicate that the structure presents columnar grains on the surface,which is transformed into equiaxed grains at the center of the casting.The average grain diameter is increased with the increase of wall thickness,and the grain distribution is consistent with the experimental results.The coincidence rate of simulated average grain diameter with the actual results reaches 80%～99%,meeting the engineering application expectation.
关键词
精密铸造/钛合金/CAFE法/组织模拟Key words
Investment Casting/Ti Alloy/CAFE Method/Microstructure Simulation引用本文复制引用
出版年
2024
NETL
NSTL
万方数据