多孔阳极氧化物的形成机理至今仍不清楚.研究者倾向于用物理模型来解释它们的生长机理,很少报道电极电位对阳极氧化的影响,因为阳极氧化电压远远高于电极电位.创新性地引入电极电位理论、氧气气泡模型以及离子电流和电子电流理论来解释3种金属(Ti、Zr和Fe)在低电压下多孔阳极氧化物的生长机理.以Ti在0.5％(质量分数)NH4F水溶液中的阳极氧化为例,计算了电极电位,解释了在低电压下多孔阳极氧化物的形貌.结果表明,多孔阳极氧化物的生长由离子电流和电子电流的比值决定.阳极氧化过程中的金属分为2类:一类是容易形成致密氧化层的金属,另一类是容易导致氧气析出的金属.相应的,电解液也被分为2类:容易形成致密氧化层的电解液和容易导致氧气析出的电解液.
Electrode Potential Explaining the Growth of Anodic Oxides
The formation mechanism of porous anodic oxides remains unclear till now.The classical field-assisted dissolution(FAD)theory cannot explain the relationship between the current curve and FAD reaction,and the influence of the electrode potential on anodization is rarely reported.The electrode potential theory,oxygen bubble model and the ionic current and electronic current theories were introduced to explain the growth of porous anodic oxides of three metals(Ti,Zr and Fe).Taking the anodization of Ti in aqueous solution containing 0.5wt％NH4F as an example,the electrode potential was calculated,and the morphology of porous anodic oxides was investigated at low voltages.Results show that the growth of porous anodic oxides is determined by the ratio of the ionic current to the electronic current.During the anodization,metals are classified into two groups:one is easy to form the compact oxide layer,and the other is easy to induce oxygen releasing,thus forming oxygen bubbles.The electrolyte is also classified into two groups correspondingly:compact oxide layer-assisted electrolyte and releasing oxygen-assisted electrolyte.

anodizationelectrode potential theoryoxygen bubble modelelectronic currentlow voltage

蒋龙飞、龚天乐、李鹏泽、张少瑜、陈滨掖、朱云暄、王冰、朱绪飞

展开 >

南京理工大学软化学与功能材料教育部重点实验室,江苏南京 210094

江苏城乡建设职业学院,江苏常州 213147

阳极氧化 电极电势理论 氧气气泡模型 电子电流 低电压

National Natural Science Foundation of ChinaNational Natural Science Foundation of ChinaNatural Science Foundation of Jiangsu Higher Education InstitutionsChangzhou Science & Technology ProgramQing Lan Project in Colleges and Universities of Jiangsu Province

515770935177709720KJB430040CJ20200026

2024

10.12442/j.issn.1002-185X.20230843

稀有金属材料与工程
中国有色金属学会,中国材料研究学会,西北有色金属研究院

稀有金属材料与工程

CSTPCD北大核心
影响因子：0.634
ISSN：1002-185X
年,卷(期)：2024.53(9)