金属拉伸试样的断口分析
Fracture Analysis of the Metal Tensile Specimen
摘要
提出了金属拉伸试样断口分析方法,讨论了试样在拉伸试验中的应力分布、断裂过程以及影响断口形貌的因素,为断裂形态分类和断裂原因分析提供了重要依据。
Abstract
In this paper,metal tensile specimen fracture analysis,tensile test specimen are discussed the stress distribution in the fracture process and the factors that affect the fracture surface,the fracture failure of a morphological classification and provides
关键词
断裂/拉伸断口/应力分布/穿晶断裂/杯锥状断口/纤维区/韧窝Key words
fracture/tensile fracture analysis/stress distribution/transgranular fracture/cup cone fracture/fiber area/dimple引用本文复制引用