17-4PH钢激光熔覆镍基碳化钨涂层工艺参数研究
Study on the Process Parameters of 17-4 PH Steel Laser Cladding Ni-Based Carbide Coating
殷铭 1王明娣2
作者信息
- 1. 苏州工业职业技术学院精密制造工程系,江苏苏州 215104;苏州大学机电工程学院,江苏苏州 215137
- 2. 苏州大学机电工程学院,江苏苏州 215137
- 折叠
摘要
通过正交试验完成16组参数熔覆试验,使用显微硬度仪、摩擦磨损仪考察不同工艺参数试样的硬度、摩擦性能,使用扫描电镜(SEM)分析和研究截面结合处形态、物相.结果表明,在选定的因素和水平情况下,送粉速度对熔覆层硬度影响最大;最佳熔覆样块显微硬度性能较基材提升了 182.9％,平均摩擦因数比基材降低了 86.7％,熔覆层和基材冶金结合性能良好.
Abstract
16 sets of parameter cladding experiments were conducted using orthogonal experiments.The hardness and friction characteristics of specimens with varying process parameters were examined using a microhardness tester and a friction wear in-strument.Additionally,the morphology and phase of cross-section joints were analyzed via scanning electron microscopy(SEM).The findings indicate that the powder delivery speed exerts the most significant influence on the cladding layer's hard-ness under the specified factors and levels.The microhardness of the optimal cladding sample is 182.9％higher than that of the substrate,resulting in an average friction factor reduction of 86.7％compared to the substrate.Moreover,there is evidence of good metallurgical bonding between the cladding layer and the substrate.
关键词
激光熔覆/17-4PH/Ni60A/正交试验/摩擦磨损Key words
laser cladding/17-4PH/Ni60A/orthogonal experiment/friction and wear引用本文复制引用