Synthesis and characterization of Al13-Oxalate gel with Keggin structure
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
国家科技期刊平台
NETL
NSTL
万方数据
In this study, the Al13-oxalate gel synthesized from Al13 solution was characterized by XRD, FTIR and MAS 27Al NMR. The results are: 1) the gel shows obvious XRD diffraction peaks, which is different from common Al gels and their oxalate precipitations; 2) the peak of AI-O stretch vibration of Al13-oxalate complexes at 810 cm-1 indicates that the gel was formed directly by the complexes, and the characteristic peaks of IR and solid-state NMR respectively occur at 725 cm-1 and ～6.1x105 chemical shift, which are respectively assigned to (Al-O)Td vibration and (Al-O)4 tetrahedron, suggesting that the gel has a unique Keggin structure; 3) Al13 polyoxocation can directly form gel with oxalate, even in a high-pH environment (=7.8). This finding provides new evidence for the universality of Al13 in natural environments. Through chemical analysis, the chemical formula of the gel was determined to be AlO4Al12(OH)24(H2O)12(C2O4)7/2.
Al13Keggin structureoxalategel
LIU Jing、ZHAO Fenghua
展开 >
The Key State Laboratory of Coal Resource & Mining Safety, China University of Mining and Technology, Beijing 100083, China
Department of Resource and Earth Science, China University of Mining and Technology, Beijing 100083, China
specialized re-search fund for the Doctoral Program of Higher Education of ChinaProgram for New Century Excellent Talents in China University of Mining and Technology
国家科技期刊平台
NSTL
万方数据