首页|碳包裹氮化铁复合材料的制备及微波吸收性能

碳包裹氮化铁复合材料的制备及微波吸收性能

扫码查看
[目的]研究不同氮化铁复合材料Fe2N@C、Fe3N@C和Fe4N@C的微波吸收性能.[方法]通过水热法合成金属有机骨架材料(MOFs),经过氮化处理得到Fe2N@C、Fe3N@C和Fe4N@C复合材料;采用X射线衍射(X-ray diffraction,XRD)、超高分辨扫描电子显微镜(scanning electron microscope,SEM)、高分辨透射电子显微镜(transmission electron microscope,TEM)、拉曼光谱(Raman spectra,Raman)和X 射线光电子能谱(X-ray photoelectron spectroscopy,XPS)等技术表征、定性Fe2N@C、Fe3N@C和Fe4N@C的结构、形貌以及成分变化,结合矢量网络分析(vector network analyzer,VNA)和振动样品磁强计(vibrating sample magnetometer,VSM)定量分析Fe2N@C、Fe3N@C和Fe4N@C对微波的反射损耗能力以及磁性能.[结果]Fe2N@C和Fe4N@C因介电常数远大于磁导率,导致阻抗匹配失衡,而Fe3N@C介电常数和磁导率相近,存在较好的阻抗匹配,涂层厚度为2 mm的样品,小于反射损耗为-10 dB的有效吸波宽带达到的频率为2.4 GHz,在频率为9.1 GHz处最小的反射损耗为-14.1 dB.[结论]3种氮化铁的相结构和碳层的缺陷程度不同,氮化铁核与碳壳的导电性不同,会在界面间出现电荷聚集,引起界面极化,导致Fe2N@C和Fe4N@C的介电常数增大,使得Fe2N@C和Fe4N@C中的介电常数远大于磁导率,最终导致阻抗匹配失衡,具有较差的吸波性能.
Preparation and microwave absorption properties of carbon-coated iron nitride composites
Objective The energy attenuation of wave-absorbing materials primarily occurs through two mechanisms:dielectric loss and magnetic loss.Conventional wave-absorbing materials are less effective because they cannot simultaneously use both electrical and magnetic losses to attenuate microwave interference.Iron nitride,characterized by magnetic properties,such as high satura-tion magnetization,low density,large surface area,and environmental friendliness,has applications in various high-tech fields.However,its widespread use is limited due to its poor dielectric loss characteristics.Carbon materials,known for their exceptional conductivity and dielectric loss properties,can be combined with iron nitride to form composite materials that exhibit both magnetic and high dielectric losses.To achieve this,metal-organic frameworks(MOFs)are used as precursors for the syn-thesis of Fe2N@C,Fe3N@C and Fe4N@C through a process involving calcination and nitriding.These core-shell wave-absorbing materials exhibit excellent stability.The incorporation of carbon increases the dielectric loss of iron nitride,generating compos-ites that exhibit high dielectric and magnetic losses,thereby improving the microwave absorption of Fe2N@C,Fe3N@C,and Fe4N@C.Further investigations will explore the microwave absorption variations between different compositions of Fe2N@C,Fe3N@C,and Fe4N@C.Methods The physical composition of Fe2N@C,Fe3N@C,and Fe4N@C was analyzed using X-Ray diffraction(XRD).Their micro-morphology was analyzed using ultra-high-resolution scanning electron microscopy(SEM)and high-resolution transmis-sion electron microscopy(TEM).The micro-morphology of Fe2N@C,Fe3N@C,and Fe4N@C was determined through the suc-cessful synthesis of carbon-encapsulated iron nitride.Raman spectroscopy and X-ray photoelectron spectroscopy(XPS)were also employed for this purpose.XPS techniques were used to characterize and investigate their conformational relationships.Microwave absorption properties,as well as the imaginary parts of the complex dielectric constant and complex permeability,were analyzed using a vector network analyzer(VNA).Their magnetic loss properties were quantified using a Vibrating Sample Magnetometer(VSM).Results and Discussion As shown in Fig.1,Fe2N,Fe3N,and Fe4N were synthesized using MOFs as precursors.Additionally,Fig.2 showed that highly dispersed Fe nanoparticles were successfully encapsulated in the carbon layer,confirming the synthe-sis of Fe2N@C,Fe3N@C,and Fe4N@C.Fig.4 showed that Fe3N@C had a relatively low degree of graphitization,resulting in a low permittivity.In contrast,Fig.6 demonstrated that Fe2N@C and Fe4N@C exhibited poor wave absorption properties,while Fe3N@C displayed good microwave absorption.Therefore,it could be concluded that Fe3N@C was a better candidate for micro-wave absorption compared to Fe2N@C and Fe4N@C.Fig.7 showed that Fe2N@C and Fe4N@C had significantly greater dielectric loss than magnetic loss due to their high imaginary dielectric constant,resulting in an imbalancd impedance matching.On the other hand,Fe3N@C had a lower imaginary dielectric constant,providing a better impedance matching due to its balanced dielectric constant and magnetic permeability.Conclusion Fe2N@C,Fe3N@C,and Fe4N@C were successfully prepared by nitriding MOFs as precursors.Fe2N@C and Fe4N@C exhibited an imbalanced impedance matching due to their dielectric constants being much higher than their magnetic permeability.In contrast,Fe3N@C had balanced values for both parameters,resulting in better impedance matching.Samples with a coating thickness of 2 mm had an effective absorbing bandwidth of less than-10 dB,with a reflection loss of-10 dB up to 2.4 GHz.The minimum reflection loss of-14.1 dB at 9.1 GHz indicated better absorbing performance.The differing electrical conductivity of the iron nitride cores and the carbon shells resulted from to the varying phase structures of the three iron nitrides and the degree of defects in the carbon layers.This difference led to charge aggregation between interfaces,causing interfacial polarization.As a result,the dielectric constants of Fe2N@C and Fe4N@C increased,exceeding their magnetic permeability and leading to an imbalanced impedance matching.

iron nitridecomposite materialsimpedance matchingmicrowave-absorption property

王文敬、董浩琪、卢洁、李伟、朱磊、郭立升、张成华、魏宇学、孙松

展开 >

安徽大学化学化工学院,安徽合肥 230601

安徽大学材料科学与工程学院,安徽合肥 230601

安徽碳鑫科技有限公司,安徽淮北 235141

氮化铁 复合材料 阻抗匹配 微波吸收

国家自然科学基金项目国家自然科学基金项目国家自然科学基金项目安徽省高校杰出青年科研项目安徽高校协同创新项目安徽省高等学校自然科学基金项目

2190200122179001221020012022AH020007GXXT-2023-0092023AH050114

2024

中国粉体技术
中国颗粒学会,济南大学,中国非金属矿工业协会矿物加工利用专业委员会

中国粉体技术

CSTPCD
影响因子:0.469
ISSN:1008-5548
年,卷(期):2024.30(3)
  • 5