首页|Mechanical properties and damage evolution characteristics of waste tire steel fiber-modified cemented paste backfill
Mechanical properties and damage evolution characteristics of waste tire steel fiber-modified cemented paste backfill
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
万方数据
During the process of constructional backfill mining,the cemented paste backfill(CPB)typically exhibits a high degree of brittleness and limited resistance to failure.In this study,the mechanical and damage evolution characteristics of waste tire steel fiber(WTSF)-modified CPB were studied through uniaxial compression tests,acoustic emission(AE)tests,and scanning electron microscopy(SEM).The results showed that the uniaxial compressive strength(UCS)decreased when the WTSF content was 0.5％,1％,and 1.5％.When the WTSF content reached 1％,the UCS of the modified CPB exhibited a minimal decrease(0.37 MPa)compared to that without WTSF.When the WTSF content was 0.5％,1％,and 1.5％,peak strain of the WTSF-modified CPB increased by 18％,31.33％,and 81.33％,while the elastic modulus decreased by 21.31％,26.21％,and 45.42％,respectively.The addition of WTSF enhances the activity of AE events in the modified CPB,resulting in a slower progression of the entire failure process.After the failure,the modified CPB retained a certain level of load-bearing capacity.Generally,the failure of the CPB was dominated by tensile cracks.After the addition of WTSF,a gradual increase in the proportion of tensile cracks was observed upon loading the modified CPB sample to the pore compaction stage.The three-dimensional localization of AE events showed that the WTSF-modified CPB underwent progressive damage during the loading,and the samples still showed good integrity after failure.Additionally,the response relation-ship between energy evolution and damage development of WTSF-modified CPB during uniaxial com-pression was analyzed,and the damage constitutive model of CPB samples with different WTSF contents was constructed.This study provides a theoretical basis for the enhancement of CPB modified by adding WTSF,serving as a valuable reference for the design of CPB constructional backfill.
Shenggen Cao、Chiyuan Che、Yun Zhang、Changhao Shan、Yang Liu、Changzheng Zhao、Shuyu Du
展开 >
State Key Laboratory for Fine Exploration and Intelligent Development of Coal Resources,School of Mines,China University of Mining and Technology,Xuzhou 221116,China
College of Energy Engineering,Xi'an University of Science & Technology,Xi'an 710054,China
National Natural Science Foundation of ChinaNational Natural Science Foundation of China
NETL
NSTL
万方数据