采用固相反应法在不同的烧结温度制备了 Sr0。55Na0。45SiO3-δ电解质材料，并通过SEM、XRD、电化学阻抗谱等方法对样品进行分析。XRD测试表明通过固相反应法在950 ℃煅烧2 h获得了纯相的Sr0。55Na0。45SiO3-δ;SEM分析和致密度的测量表明Sr0。55Na0。45SiO3-δ具有良好的烧结性能，在1000 ℃烧结2 h后相对密度达到99％以上;电化学阻抗谱分析表明Sr0。55Na0。45SiO3-δ具有良好的电性能，在600 ℃和800 ℃温度测试下的电导率分别为0。01501 S·cm-1和0。0677 S·cm-1，0。75 eV的电导活化能。研究表明制备的材料具备成为中温固体氧化物燃料电池理想电解质材料之一。
Preparation and Performance of Sr0.55Na0.45SiO3-δ Solid Electrolyte
In this work,Sr0.55Na0.45SiO3-δ electrolyte material was prepared by the solid state reaction method at different sintering temperatures,and the samples were analyzed by SEM,XRD,and electrochemical impedance spectroscopy.The XRD results show that pure-phase Sr0.55Na0.45SiO3-δ was obtained by the solid-state reaction method at 950 ℃ for 2 h.The SEM analysis and density determination showed that Sr0.55Na0.45SiO3-δ have good sintering performance,with a relative density exceeding 99％after sintering at 1000 ℃ for 2 h.Electrochemical impedance spectroscopy analysis revealed that Sr0.55Na0.45SiO3-δ has excellent electrical performance,with conductivity of 0.01501 S·cm-1 and 0.0677 S·cm-1 at 600 ℃ and 800 ℃,respectively,and conductivity activation energy of 0.75 eV.The study suggests that the materials prepared in this paper have the potential to be ideal electrolyte materials for intermediate-temperature solid oxide fuel cells(IT-SOFCs).

ElectrolyteSOFCsConductivitySrSiO3

陈超、赵浩勇、曹志坤、朱民正、曾桄纳、田长安

展开 >

韶关学院化学与土木工程学院,韶关 512005

合肥学院能源材料与化工学院,合肥 230601

电解质 SOFCs 电导率 SrSiO3

广东省基础与应用基础研究基金广东省基础与应用基础研究基金广东省教育厅科技项目广东省教育厅科技项目广东省教育厅科技项目韶关市科技计划韶关学院科技项目韶关学院大学生创新项目

2021A15150106712020A15150112212021ZDJS0712021KTSCX1222022KQNCX077210724134530330SZ2020KJ03Sycxcy2023140

2024

10.16521/j.cnki.issn.1001-9642.2024.06.004

中国陶瓷
中国轻工业陶瓷研究所

中国陶瓷

北大核心
影响因子：0.376
ISSN：1001-9642
年,卷(期)：2024.60(6)
  • 12