首页|TEM study on microstructures and properties of 7050 aluminum alloy during thermal exposure
TEM study on microstructures and properties of 7050 aluminum alloy during thermal exposure
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
万方数据
The microstructures of 7050 aluminum alloy under different thermal exposure conditions were investigated by means of transmission electron microscopy (TEM),high resolution electron microscopy (HREM) and tensile test.Guinier preston (GP) zone and η' phase are the main precipitates in original 7050 alloy.The orientation relationship between η' and matrix is [0001].//[1(1)1]Al and (10(1)0)η'.//(110)A1.When the alloy is exposed at different temperatures for 500 h,with the thermal exposure temperature increasing,it can be seen under TEM that the precipitates become larger and the width of precipitate free zones (PFZ) becomes larger.The higher temperature the alloy is exposed at,the more the strength is reduced.Both GP zones and η' precipitates getting coarser and the PFZ getting wider should be responsible for the strength decline and elongation rise of 7050 alloy during thermal exposure.
7050 aluminum alloythermal exposuremicrostructure
SHEN Kai、CHEN Jin-ling、YIN Zhi-min
展开 >
School of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
School of Materials Science and Engineering, Central South University, Changsha 410083, China