采用锁孔型钨极氩弧焊(K-TIG)在不同热量输入条件下焊接厚度为12 mm的Ti-6Al-4V(TC4)钛合金板,并研究焊缝金属区(WMZ)的显微组织、晶界特征及力学性能.实验结果表明:当输入热量为2.30～2.62 kJ/mm时,K-TIG焊缝成形良好,未出现明显的缺陷;当热输入逐渐增加时,α板条的长度增加,α'相和残余β相减少.电子背散射衍射(EBSD)测试结果表明:WMZ中的大角度晶界比例随着热量输入的增加而增加.当热量输入从2.30增加到2.62 kJ/mm时,WMZ的抗拉强度逐渐降低,伸长率增加.WMZ的冲击韧性随着热量输入的增加而增加.
Microstructure and mechanical properties of TC4 titanium alloy K-TIG welded joints
The 12 mm-thick Ti-6Al-4V (TC4) titanium alloy plates were welded using keyhole tungsten inert gas (K-TIG) welding at various heat inputs. The microstructure, grain boundary (GB) characteristics and mechanical properties of the weld metal zone (WMZ) were analyzed. The test results show that the K-TIG welds are well formed, and no obvious defects are observed when the heat input is 2.30-2.62 kJ/mm. When the heat input gradually increases, α laths increase in length, and α' phase and residual β phase are reduced. The electron backscatter diffraction (EBSD) test results indicate that the high-angle GB proportion in the WMZ increases with the increase of heat input. The tensile strength of the WMZ gradually decreases and the elongation of the WMZ increases when the heat input increases from 2.30 to 2.62 kJ/mm. The impact toughness of the WMZ increases as the heat input increases.

K-TIG weldingheat inputα' phasehigh-angle grain boundaryCharpy impact fracture surface

崔书婉、石永华、张程士

展开 >

广西科技大学机械与交通工程学院,柳州 545006

华南理工大学机械与汽车工程学院,广州 510640

柳州上汽汽车变速器有限公司,柳州 545006

K-TIG焊接 热量输入 α'相 大角度晶界 夏比冲击断裂面

authors are grateful for the financial supports from the Key Research and Development Program of Guangdong Province, ChinaNatural Science Foundation of Guangdong Province, ChinaScience and Technology Base and Talent Special Project of Guangxi Province, ChinaGuangxi University of Science and Technology Doctoral Fund, China

2020B0909280032020A1515011050AD1924515019Z27

2021

10.1016/S1003-6326(21)65506-1

中国有色金属学报(英文版)
中国有色金属学会

中国有色金属学报(英文版)

CSTPCDCSCDSCI
影响因子：1.183
ISSN：1003-6326
年,卷(期)：2021.31(2)
  • 7
  • 4