首页|Ti49.2Ni50.8合金在等径角挤压过程中Ti3Ni4析出相的演化规律

Ti49.2Ni50.8合金在等径角挤压过程中Ti3Ni4析出相的演化规律

扫码查看
采用透射电子显微镜研究Ti49.2Ni50.8合金中Ti3Ni4析出相在等径角挤压及中间退火过程中的演化规律.固溶态Ti49.2Ni50.8合金在450℃时效处理10~60 min以获得尺寸为37~75 nm的Ti3Ni4析出相.在450℃等径角挤压处理1道次后,时效处理10 min和30 min试样中Ti3Ni4析出相完全溶解;而在时效处理60 min试样中Ti3Ni4析出相尺寸减小.Ti3Ni4析出相完全溶解的临界尺寸范围为37~68 nm.等径角挤压态试样的位错密度取决于Ti3Ni4析出相的初始尺寸.随初始时效时间从10 min延长至60 min,试样的位错密度先增加然后降低.
Evolution of Ti3Ni4 precipitates in Ti49.2Ni50.8 alloy during equal channel angular pressing
The evolution of Ti3Ni4 precipitates in Ti49.2Ni50.8 alloy during equal channel angular pressing (ECAP) and intermediate annealing was investigated by transmission electron microscopy. The solution-treated Ti49.2Ni50.8 alloy was aged at 450 ℃ for 10 to 60 min to obtain Ti3Ni4 precipitates ranging from 37 to 75 nm. After ECAP at 450 ℃ for one pass, Ti3Ni4 precipitates introduced by aging for 10 and 30 min totally dissolve into the matrix; however, those produced by aging for 60 min become smaller. The critical size of Ti3Ni4 precipitates to totally dissolve into matrix is determined to be in the range of 37-68 nm. The dislocation density of ECAP-processed samples depends on the initial size of Ti3Ni4 precipitates after aging. With increasing the duration of initial aging from 10 to 60 min, the dislocation density firstly increases and then decreases.

TiNi shape memory alloyequal channel angular pressingdislocationprecipitationTi3Ni4 phase

任佳瑞、Alexander V.SHUITCEV、孙斌、陈枫、李莉、佟运祥

展开 >

哈尔滨工程大学 材料科学与化学工程学院 材料加工及智能制造研究所,哈尔滨 150001

哈尔滨工程大学 材料科学与化学工程学院 分析测试中心,哈尔滨 150001

TiNi形状记忆合金 等径角挤压 位错 析出 Ti3Ni4相

National Natural Science Foundation of ChinaNational Key R&D Program of China

516710642017YFE0123500

2021

中国有色金属学报(英文版)
中国有色金属学会

中国有色金属学报(英文版)

CSTPCDCSCDSCI
影响因子:1.183
ISSN:1003-6326
年,卷(期):2021.31(4)
  • 1
  • 2