首页|Al-Cu-Li-Mg合金纳米相之间溶质配分行为的第一性原理研究

Al-Cu-Li-Mg合金纳米相之间溶质配分行为的第一性原理研究

扫码查看
原文链接
  • NETL
  • NSTL
  • 万方数据
采用一性原理计算考察25种合金化元素在大多数商业牌号Al-Cu-Li-Mg合金中主要纳米相(δ'-Al3Li、θ-Al2Cu、T1-Al6Cu4Li3和S-Al2CuMg)之间的溶质配分能和配分行为.计算结果表明,主合金化元素Li不能直接影响θ'和S相,Cu不能直接影响δ'相,Mg不能直接影响θ'和δ相,但可以较弱地固溶于T1相.对于微合金化元素,Si是唯一一种可以固溶于4种纳米相的元素.Au能固溶于δ'、θ'和S相,Cd能固溶于δ'、T1和S相,Zr能固溶于δ和T1相,Ni仅有微弱的趋势固溶于θ'和S相.Ti、V、Zn、Ag和Mo只能固溶于δ'相,而Cr、Mn、Fe和Co对这4种纳米相均没有直接影响.几乎所有的稀土元素均能强烈固溶于T1、δ'和S相,但无法固溶于θ相.仅Sc略显特殊,对S相没有明显的固溶趋势.计算预测的溶质配分能构成了一个原型数据库,有利于指导和加速Al-Li合金及其他相关Al合金的设计.
First-principles insights into solute partition among various nano-phases in Al-Cu-Li-Mg alloys
First-principles energetics calculations were performed over a group of 25 candidate elements,to investigate their partition energies and behaviors among major nano-phases(δ'-Al 3 Li,θ'-Al2Cu,T1-Al6Cu4Li3 and S-Al2CuMg)in most commercial Al-Cu-Li-Mg alloys.It was revealed that principal alloying element Li cannot directly affect θ'and S,Cu cannot directly affect δ',Mg cannot directly affect θ'and δ'but can weakly partition into T1.As for micro-alloying elements,Si is the only element that can partition into all the four nano-phases.Au can partition into δ',θ'and S.Cd can partition into δ',T1 and S.Zr can partition into δ'and T1.Ni substitution can weakly partition into θ'and SS.Ti,V,Zn,Ag and Mo can partition into δ'only.Cr,Mn,Fe and Co cannot directly affect any of the four nano-phases.Almost all RE-elements can strongly partition into T1,δ'and S,but would be expelled by θ'.Only Sc is somehow particular to S,showing no partition preference in S.The newly obtained fundamental results could constitute a simple prototype database in support for the accelerated design of Al-Li based alloys and other related Al alloys.

Al-Cu-Li-Mg alloynano-phasemicro-alloyingsolute partitionfirst-principles

刘正卿、江勇、王怡人、姚建刚

展开 >

中南大学材料科学与工程学院,长沙 410083

烟台南山学院材料科学与工程学院,烟台 265713

中南大学粉末冶金国家重点实验室,长沙 410083

Al-Cu-Li-Mg合金 纳米相 微合金化 溶质配分 第一性原理

National Science Foundation of ChinaNatural Science Foundation of Shandong Province,ChinaScience and Technology Planning Project of Longkou City,China

51971249ZR2020KE0122021KJJH025

2024

10.1016/S1003-6326(24)66503-9

中国有色金属学报(英文版)
中国有色金属学会

中国有色金属学报(英文版)

CSTPCD
影响因子：1.183
ISSN：1003-6326
年,卷(期)：2024.34(6)
  • 5