TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43％reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500 ℃ displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845％.
关键词
TA1/P-Ti/AA6061复合板/氧化处理/退火处理/冷轧复合
Key words
TA1 P-Ti/AA6061 composite plate/oxidation treatment/annealing treatment/cold roll bonding
引用本文复制引用
基金项目
National Natural Science Foundation of China(52075472)
National Natural Science Foundation of China(52004242)
National Key Research and Development Program of China(2018YFA0707300)
Natural Science Foundation of Hebei Province,China(E2020203001)
万方数据