Microstructure and properties of LZQT600-3 HCCDIBs for plunger pump cylinder

扫码查看
原文链接
  • 万方数据
  • 维普
It is important to improve the comprehensive performance of the ductile iron bars(DIBs)for the cylinder block of the extra high pressure hydraulic plunger pump and accelerate the industrial application.In this work,the LZQT600-3 DIBs with the diameter of 145 mm were prepared by the horizontal continuous casting(HCC)process,that is,LZQT600-3 HCCDIBs.The microstructure and room temperature tensile properties of different sections[left-edge(surface layer),left-1/2R(left half of the radius),and the center of the HCCDIBs]were studied.The results show that the spheroidization of LZQT600-3 HCCDIBs matrix from the left-edge,left-1/2R to the center is at nodulizing grade II and above.As the cooling rate gradually decreases from surface to the center of the HCCIBs,the number of spheroidized graphite is gradually reduced,the size is gradually increased,the shape factor is decreased,and the pearlite content and lamellate spacing are increased.Along the horizontal direction of the section,the hardness of the material is distributed symmetrically around the center of the HCCDIBs.In the vertical direction,the hardness distribution in the center of the HCCDIBs is asymmetrical due to the gravity during the solidification process.Therefore,the microstructure in the lower part of the section solidifies relatively quickly.The left-edge has the best tensile mechanical properties,and the ultimate tensile strength,yield tensile strength and elongation are 597.3 MPa,418.5 MPa and 9.6%,respectively.The tensile fracture belongs to the ductile-brittle hybrid fracture.The comprehensive performances of LZQT600-3 HCCDIBs meet the actual application requirements of ultra-high pressure hydraulic plunger pump cylinder.

horizontal continuous casting(HCC)nodular cast ironductile iron barsmicrostructuremechanical properties

Chun-jie Xu、Yuan-ying Jin、Dong Ma、Zhen Zhao、Jia-wei Qi、Shang Sui、Xiang-quan Wu、Can Guo、Zhong-ming Zhang、Yong-hui Liu、Dan Shechtman

展开 >

School of Materials Science and Engineering,Xi'an University of Technology,Xi'an 710048,China

Xi'an Shechtman Nobel Prize New Materials Institute,Xi'an 710048,China

Tongchuan Huazhu Precision Technology Co.,Ltd.,Tongchuan 727100,Shaanxi,China

Faculty of Materials Science and Engineering,Technion-Israel Insititue of Technology,Haifa 3200003,Israel

展开 >

International Science and Technology Cooperation Program of Shaanxi ProvinceProjects of Major Innovation Platforms for Scientific and Technological and Local Transformation of Scientific and TechnologProjects of Major Scientific and Technological Achievements Local Transformation of Xi'anHigher Education Institution Discipline Innovation and Intelligence Base of Shaanxi Provincial

2023-GHZD-5020GXSF00032022JH-ZDZH-0039S2021-ZC-GXYZ-0011

2024

10.1007/s41230-024-3061-6

中国铸造
沈阳铸造研究所

中国铸造

CSTPCDEI
影响因子：0.299
ISSN：1672-6421
年,卷(期)：2024.21(2)
  • 20