磷酸盐干态覆膜砂结块现象的改善措施研究
Study on the Amelioration Measures for the Caking Phenomenon of Phosphate Dry Coated Sand
罗圆圆 1夏露 1张友寿 1夏增权 1胡汉基1
作者信息
- 1. 湖北工业大学材料与化学工程学院,湖北武汉 430068;绿色轻工材料湖北省重点实验室,湖北武汉 430068
- 折叠
摘要
结块现象是磷酸盐干态覆膜砂在保存中遇到的问题之一,难以使覆膜砂保持散砂状态,从而严重影响了覆膜砂的流动性,阻碍了无机覆膜砂的应用.通过向干态覆膜砂里加入偶联剂和干燥剂以改善结块问题,结果表明:将偶联剂处理前、后的两种干态覆膜砂以质量比为1∶1混合均匀,再加入占覆膜砂质量分数为1/200的硅胶干燥剂,能有效改善覆膜砂结块问题,结块率下降65％左右,射砂成形所得试样的抗拉强度达到1.5 Mpa以上.
Abstract
Caking phenomenon is one of the problems encountered in the preservation of phosphate dry coated sand.It is difficult to keep the coated sand in the state of loose sand,which seriously affects the fluidity of the coated sand and the application of inorganic coated sand.In this paper,the caking problem was ameliorated by adding coupling agent and silica-gel drier to dry coated sand.The results showed that the two kinds of dry coated sand before and after coupling agent treatment were mixed uniformly with a mass ratio of 1∶1,and then added the silica-gel drier with a mass fraction of 1/200,which could effectively ameliorate the caking problem,the caking rate decreased about 65％,and the tensile strength of the sample obtained by sand-shooting was more than 1.5 Mpa.
关键词
磷酸盐干态覆膜砂/偶联剂/硅胶干燥剂/结块率/抗拉强度Key words
phosphate dry coated sand/coupling agent/silica-gel drier/caking rate/tensile strength引用本文复制引用