首页|Thermodynamic Calculation of Carbide Precipitate in Niobium Microallloyed Steels
Thermodynamic Calculation of Carbide Precipitate in Niobium Microallloyed Steels
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
On the basis of regular solution sublattice model, thermodynamic equilibrium of austenite/carbide in Fe-Nb-C ternary system was investigated. The equilibrium volume fraction, chemical driving force of carbide precipitates and molar fraction of niobium and carbon in solution at different temperatures were evaluated respectively. The volume fraction of precipitates increases, molar fraction of niobium dissolved in austenite decreases and molar fraction of carbon increases with decreasing the niobium content. The driving force increases with the decrease of temperature, and then comes to be stable at relatively low temperatures. The predicted ratio of carbon in precipitates is in good agreement with the measured one.
microalloyed steelthermodynamic calculationphase equilibriumcarbideprediction model
XU Yun-bo、YU Yong-mei、LIU Xiang-hua
展开 >
State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China
NETL
NSTL